硅酸盐学报

轻骨料对混凝土自养护减缩效率的影响

作者：董淑慧张宝生葛勇袁杰

单位：哈尔滨工业大学

关键词：轻骨料自养护自收缩预湿程度减缩效率

分类号：TU528.2

出版年,卷(期):页码：2009,37(3):465-469

DOI：

摘要：

通过测试不同配合比轻骨料混凝土的早期自收缩与长期干缩行为,研究轻骨料性能对混凝土自养护减缩效率的影响。结果表明:陶粒的预湿程度与释水能力对于混凝土自养护减缩效率的影响显著;随着预湿程度的增加早期自收缩减小,自养护减缩效率提高;饱和预湿的宾县页岩陶粒自养护减缩效率为39.1%,陶砂影响规律与其相似,但效率更高。实验中采用130kg/m3掺量的饱和预湿陶砂,自养护减缩效率可达95.6%。

The autogenous shrinkage at early age and drying shrinkage of lightweight aggregate concrete with different mix proportions were measured,and the influence of lightweight aggregate in concrete on the shrinkage reduction efficiency due to internal curing was studied.The results indicate that the absorption-desorption rate and the degree of pre-wetting of ceramsite have a significant impact on the shrinkage reduction efficiency of concrete.With the increase of pre-wetting of ceramsite,the autogenous shrinkage of high performance lightweight concrete decreases,and the shrinkage reduction efficiency improves;it is about 39.1% for the saturated Binxian ceramsite.The ceramsite sand has a similar effect;it has greater shrinkage reduction efficiency,which reached 95.6% for the saturated ceramsite sand at the dosage of 130 kg/m3.

基金项目：

交通部西部交通建设科技(200331882008)资助项目

作者简介：

参考文献：

[1]丁庆军.高强次轻混凝土研究与应用[D].武汉理工大学,武汉:武汉理工大学,2006.DING Qingjun.Research on high strength semi-lightweighe concrete and it's application(in Chinese,dissertation).Wuhan:Wuhan Univer-sity of Technology,2006. [2]BENTZ Dale P,HALLECk Phillip M,GRADER Abraham S,et al.Concrete international water movement during internal curing direct observation using X-ray microtomo grathy[J].Concr Int,2006,10:39-46. [3]IGARASHIL Shin-Ichi.Autogenous shrinkage and induced restraining stresses in high strength concretes[J].Cem Concr Res,2000,30:1701-1707. [4]LI Jianyong,YAO Yan.A study on creep and drying shrinkage of high performance concrete[J].Cem Concr Res,2001,31:1203-1206. [5]BALOGH Anne.New admixture combats concrete shrinkage[J].Concr Int,1996(7):142-146. MEHTA P K.The relation between micro-structure and performance in hardened cement paste[A]//The eighth international cement confer-ence[C].New Jersey,USA,1987:243-246. [7]DONG Shuhui,GE Yong,YUAN Jie,et al.Study on shrinkage pro perty of lightweight aggregate concrete[J].Concrete,2008,(2):47-49. [8]LOUKILI Ahmed,CHOPIN David,KHELIDJ Abdelhafid,et al.A new aproach to determine autogenous shrinkage of mortar at an early age considering temperature history[J].Cem Concr Res,2000,(30):915-922. [9]HOLT Erika E.Early age autogenous shrinkage of concrete[D].Was hington:Philosophy University of Washington,2001:117-165. [10]CHEN Gengxin,LIU Xunbo.Study on testing method of LWAs'elastic modul[J].Build Mater Applicat,2000(2):36-38. [11]MOKAREM David W.Development of concrete shrinkage perfor mance specifications[R].Virginia Transportation Research Council,2002:134-135. [12]HUA C,ACKER P,EHRACHER A.Analyses and models of the autogeneous shrinkage of hardening cement pastegraduate student for master degree[J].Cem Concr Res,1995,25(7):1457-1468.

服务与反馈：

【文章下载】【加入收藏】