工程应力分布玻璃研究进展
作者:许杰 吴云龙 赵芳红 张保军 马眷荣  
单位:中国建筑材料科学研究总院玻璃科学研究所  
关键词:工程应力分布玻璃  两步离子交换  强度  稳定性 
分类号:TQ171.1
出版年,卷(期):页码:2009,37(12):2135-2141
DOI:
摘要:

工程应力分布(engineered stress profile,ESP)玻璃作为一种新型的增强玻璃引起了研究人员的广泛关注。综述了ESP玻璃的理论基础,介绍了ESP玻璃的几种制造工艺及其力学性能。总结了ESP玻璃较传统增强玻璃的优点:强度高,强度分散性低,抗表面损伤能力强及断裂前出现多重裂纹。针对ESP的研究现状,提出了ESP玻璃今后的研究方向:综合其它玻璃增强方法提高玻璃强度,采用微波混合加热或者电场辅助离子交换以缩短处理时间,降低工艺成本。

how to cheat women who want to cheat wife cheat story
online click open
read percentage of women who cheat signs of infidelity
printable coupons for cialis drug discount coupons coupon for free cialis

As a novel strengthened glass, engineered stress profile (ESP) glass has attracted extensive attention during recent years. The theoretical basis of the ESP glass was reviewed. The processing and mechanical properties of some ESP glasses were introduced. Compared with the conventional strengthened glass, the merits of the ESP glass (such as high strength, low strength variability, high surface damage resistance and multiple cracking before final failure) were outlined. The combination with other strengthening methods to improve glass strength and microwave hybrid heating or electric field assisted ion exchange used to shorten treatment time and lower cost for processing were proposed to be some aspects on the studies of ESP glass in the future.

read cheat on husband signs of infidelity
bystolic copay card click bystolic coupon voucher
基金项目:
科技部国际科技合作项目(2005DFBA0009)资助
作者简介:
how to cheat women who want to cheat wife cheat story
why women cheat on husbands online link
online read here open
open click here go
my husband cheated on me men who have affairs women who cheat on husband
amoxicillin amoxicillin amoxicillin
参考文献:

[1]BARTENEV G M,SANDITOV D S.The strength and some mechani-cal characteristics of high-strength glasses[J].J Non-Cryst Solids,1982,48:405–421. [2]GRIFFITH A A.The phenomena of rupture and flow in solids[J].Phil Trans Roy Soc,1920,A221:163–198. [3]GRIFFITH A A.Theory of rupture[A]//Proceedings of the First Int ernational Conference for Applied Mechanics[C].Delft,Netherlands,1924:55–63. [4]VARSHNEYA A K.Kinetics of ion exchange in glasses[J].J Non-Cryst Solids,1975,19:355–365. [5]KELLMAN C.The how and why of chemically strengthened glass[J].Glass Ind,1993,6:23–27. [6]GY R.Ion exchange for glass strengthening[J].Mater Sci Eng B,2008,149(2):159–165. [7]BECK R J.Strength variability of ion-exchanged glass[D].Pennsyl-vania:Pennsylvania State University,University Park,1989. [8]TERVONEN A,POYHONEN P,HONKANEN S,et al.Examination of two-step fabrication methods for single-mode fiber compatible ion-exchanged glass waveguides[J].Appl Opt,1991,30(3):338–343. [9]TERVONEN A,HONKANEN S.Model for waveguide fabrication in glass by two-step ion exchange with ionic masking[J].Opt Lett,1988,13:71–78. [10]GREEN D J,TANDON R,SGLAVO V M.Crack arrest and multiple cracking in glass through the use of designed residual stress profiles[J].Science,1999,283(5406):1295–1297. [11]GLASS S J,BEAUCHAMP E K,NEWTON C,et al.Strength,fracture behavior and stress profiles for engineered stress profile(ESP)glass[A]//102nd Annual Meeting of the American Ceramic Society[C],2000. [12]GREEN D J.An introduction to mechanical properties of ceramics[M].Cambridge:Cambridge University Press,1998:285–315. [13]COOK R F,CLARKE D R.Fracture stability,R-curves and strength variability[J].Acta Metall,1988,36(3):555–562. [14]SHETTY D K,WANG J S.Crack stability and strength distribution of ceramics that exhibit rising crack-resistance(R-curve)behavior[J].J Am Ceram Soc,1989,72(7):1158–1162. [15]GREEN D J,MALONEY B R.Influence of surface stress on indenta-tion cracking[J].J Am Ceram Soc,1986,69(3):223–225. [16]SCHAEFFER H A.Thermal and chemical strengthening of glass—review and outlook[A]//KERKJIAN C R ed.Strength of Inorganic Glass[C].New York:Plenum Press,1985:469–483. [17]TANDON R,GREEN D J.Crack stabilization under the influence of residual compressive stress[J].J Am Ceram Soc,1991,74(8):1981–1986. [18]TANDON R,GREEN D J.The effect of crack growth stability induced by residual compressive stresses on strength variability[J].J Mater Res,1992,7(3):765–771. [19]TANDON R,GREEN D J,COOK R F.Strength variability in brittle materials stabilizing and destabilizing resistance fields[J].Acta Metall Mater,1993,41(2):399–408. [20]SGLAVO V M,LARENTIS L,GREEN D J.Flaw-insensitive ion-exchanged glass:I,theoretical aspects[J].J Am Ceram Soc,2001,84(8):1827–1831. [21]GREEN D J.Critical parameters in the processing of engineered stress profile glasses[J].J Non-Cryst Solids,2003,316:35–41. [22]SHEN J,GREEN D J,PANTANO C G.Control of concentration profile in two step ion exchanged glasses[J].Phys Chem Glasses,2003,44(4):284–292. [23]SHEN J,GREEN D J.Prediction of stress profiles in ion exchanged glasses[J].J Non-Cryst Solids,2004,344:79–87. [24]SGLAVO V M,GREEN D J.Flaw-insensitive ion-exchanged glass:II,production and mechanical performance[J].J Am Ceram Soc,2001,84(8):1832–1838. [25]ABRAMS M B,GREEN D J,GLASS S J.Fracture behavior of engi-neered stress profile soda lime silicate glass[J].J Non-Cryst Solids,2003,321:10–19. [26]SHEN J,GREEN D J.Variable-temperature ion-exchanged engineered stress profile(ESP)glass[J].J Am Ceram Soc,2003,86(11):1979–1981. [27]SGLAVO V M,PREZZI A,ALESSANDRINI M.Processing of glasses with engineered stress profiles[J].J Non-Cryst Solids,2004,344:73–78. [28]SGLAVO V M,PREZZI A,ZANDONELLA T.Engineered stress-profile silicate glass:high strength material insensitive to surface de-fects and fatigue[J].Adv Eng Mater,2004,6(5):344–349. [29]SHEN J,GREEN D J,TRESSLER R E.Stress relaxation of a soda lime silicate glass below the glass transition temperature[J].J Non-Cryst Solids,2003,324:277–288. [30]DONALD I W.Review:methods for improving the mechanical prop-erties of oxide glasses[J]J Mater Sci,1989,24:4177–4208. [31]付静.玻璃表面微缺陷与玻璃表面改性研究[D].北京:中国建筑材料科学研究院,2001.FU Jing.Analysis of micro-cracks of glass surface and ion-exchanged surface modification(in Chinese,dissertation).Beijing:China Building Materials Academy,2001. [32]BEAUCHAMP E K.Fracture behavior of double-ion-exchanged glass[J].Ceram Trans,2001,122:1–20. [33]ABRAMS M B,GREEN D J.Prediction of crack propagation and fracture in residually stressed glass as a function of the stress profile and flaw size distribution[J].J Eur Ceram Soc,2006,26:2677–2684. [34]ABRAMS M B,GREEN D J.Prediction of stable crack growth ge-ometry in residually stressed glass[J].Int J Fracture,2004,130:601–615. [35]SGLAVO V M,PREZZI A,GREEN D J.In situ observation of crack propagation in ESP(engineered stress profile)glass[J].Eng Fract Mech,2007,74:1383–1398.

online want my wife to cheat married woman looking to cheat
why married men cheat on their wives women cheat on men
abortion las vegas period after abortion abortion pictures
sumatriptan side effects sumatriptan side effects sumatriptan side effects
服务与反馈:
文章下载】【加入收藏
中国硅酸盐学会《硅酸盐学报》编辑室
京ICP备10016537号-2
京公网安备 11010802024188号
地址:北京市海淀区三里河路11号    邮政编码:100831
电话:010-57811253  57811254    
E-mail:jccs@ceramsoc.com