高分子网络凝胶法制备纳米氧化锌的工艺控制(英文)

作者：吴建锋刘孟方斌正张锋意赵娜徐晓虹

分类号：TB383.1

出版年,卷(期):页码：2009,37(10):1782-1790

DOI：

摘要：

以乙酸锌[Zn(Ac)2]为原料,丙烯酰胺(AM)为单体,N,N’-亚甲基双丙烯酰胺(MABM)为网络剂,采用高分子网络凝胶法制备了纳米ZnO粉体,研究了其制备过程中反应物浓度、引发剂(NH4)2S2O8含量、溶液的pH值及各反应条件对纳米ZnO晶粒尺寸的影响。X射线衍射分析结果表明:纳米ZnO颗粒的平均晶粒大小随Zn2+起始浓度及引发剂含量的增加而增加,随溶液pH值的增加而减小。确定了用高分子网络凝胶法制备纳米ZnO粉体的最佳工艺参数为:反应温度80℃;反应时间2h;干燥温度100℃;干燥时间4h。

Nanosized ZnO powders were synthesized from zinc acetate by a polyacrylamide-gel method.Acrylamide and N,N'-methylenebisacrylamide were used in the synthesis as a monomer,and a network reagent,respectively.The effects of the parameters(such as reactant concentration,content of reaction initiator(NH4)2S2O8,pH value of solvent,etc.) on the properties of the nanosized ZnO powders were investigated.The crystalline characteristics of the powders was determined by X-ray diffraction.The results indicate that the nanosized ZnO all belong to a hexagonal structure,and the average crystalline grain size decreases with the decreasing of reactant concentration and the reaction initiator content and increasing pH value.In addition,the synthesis process parameters can be optimized at the reaction temperature of 80 ℃ for 2 h and drying at 100 ℃ for 4 h.

基金项目：

国家支撑计划(2008ACB41B00)资助项目

作者简介：

参考文献：

[1] JI Minxia,LIU Liqiang,WANG Shufeng. Effect on nanometer zinc oxide powders size under sol preparation condition [J]. New Mater Exploitat Res (in Chinese),2005 (8): 55-57. [2] YIN Hairong,WANG Minghua,LIU Gang. Application of polyacryla- mide gel method preparing nanometer powders [J]. Ceramics (in Chi- nese),2006 (8): 10-12. [3] DOUY A,ODIER P. Preparation of nanoscale YBa2Cu3O7-x powder by the polyacrylamide gel method nanostructured materials [J]. Mater Res Bull (in Chinese),1989,24(10): 119-123. [4] JIANG Tao,SHAO Zhongbao,MA Guofeng. Preparation of nanome- ter-sized SrCe0.90Y0.10O2.95 powders by polyacrylamide gel method. Non-Ferrous Mining Metall (in Chinese),2004,20(4): 45-47. [5] LIU Shengfeng,WU Chunyan,HAN Xiaozhao. Preparation of nano- scale NiO powders by polymer-network gel process [J]. Chin J Inorg Chem (in Chinese),2003,19(6): 624-626. [6] SHAO Zhongbao,LI Guorong. Preparation of nanometer-sized zinc oxide powders by polyacrylamide gel method [J]. Chin J Mater Res (in Chinese),2001,15(6): 681-685 [7] HAN Jing,YANG Qiyan,SHI Liyi,et al. Study on the photocatalytic properties of composite thin film based on nanometer ZnO/PVAc [J]. Chemistry (in Chinese),2008 (4): 292-296. [8] YUAN Jiren,LI Yaoqiu,DENG Xinhua. Influence of particle size and shape on light absorbability of nanometer ZnO. J Hebei Polytech Univ (Nat Sci Ed,in Chinese),2007,29(4): 134-135. [9] SHAN Yingmin,MUNIRE Albudukelimu,CAO Ruixiu. Solution polymerization of polyacrylamide with controllable molecular weight [J]. Thermosetting Resin,2007,22(4): 6-9. [10] SHAO Z B,WANG C Y,GENG S D,et al. Fabrication of nanome- ter-sized zinc oxide at low decomposing temperature [J]. J Mater Proc Technol (in Chinese),2006,178: 247-250. [11] VAFAEE M,SASANI M. Preparation and characterization of ZnO nanoparticles by a novel sol-gel route [J]. Mater Lett (in Chinese), 2006 (1): 1-4. [12] WU Danglan,FANG Yi,CHEN Riyao,et al. Studies on polyacryla- mide synthesis [J]. Contemporary Chem Ind (in Chinese),2005,34(3): 183-187.

服务与反馈：

【文章下载】【加入收藏】