硅酸盐学报

多晶Ce∶YIG粉体的制备、结构与磁性研究

作者：王巍兰中文王豪才

单位：电子科技大学微电子与固体电子学院电子科技大学微电子与固体电子学院电子科技大学微电子与固体电子学院成都610054 西南交通大学成都610031 成都610054 成都610054

分类号：TQ174

出版年,卷(期):页码：2003,31(6):566-570

DOI：

摘要：

用共沉淀法制备了纳米级的Ce∶YIG(yttriumirongarnet)石榴石粉体颗粒。所制备粉体颗粒中各种元素分布均匀 ,颗粒的粒径分布范围窄 ,粉体的团聚程度小。DTATG曲线显示 :粉体中Ce∶YIG晶相的形成温度在 75 2～ 846℃这一范围内。XRD的结果表明 :在 95 0℃烧结 1h即可得到Ce∶YIG颗粒 ,然而始终有部分Ce4+ 离子以CeO2 的形式存在 ,未能进入Ce∶YIG晶相结构。粉体饱和磁化强度随烧结温度的不同而变化 ,在 10 0 0℃时的比饱和磁化强度为 17.0 1(A·m2 ) /kg。

Cerium doped yttrium iron garnet powder in nanometer size was prepared by coprecipitation method. It is found that elements of Y, Ce and Fe are uniformly distributed in the powder and slight agglomeration formation is observed. DTATG results show that phase transition temperature from oxide to crystalline cubic Ce∶YIG begins at 752 ℃ and ends at 846 ℃. After calcination at 950 ℃ for 1 h, Ce∶YIG phase can be obtained and no other phase is found during the whole sintering process. But not reacted CeO 2 is still observed in XRD patterns. The saturation magnetization of powder is changed with the sintering temperature, which reaches to 17.01( A·m 2)/ kg at 1 000 ℃.

基金项目：

作者简介：

参考文献：

[1]TAMAKIT ,TSUSHIMAK .Growthof(GdBi)3Fe5O12 bulksinglecrystalsanditsapplicationtoanopticalisolator[J].JMagnSocJpn,1987,11:173—176. [2]GOMIM ,FURUYAMAH ,ABEM .Strongmagneto opticalenhance mentinhighlyCe substitutedirongarnetfilmspreparedbysputtering[J].JApplPhys,1991,70(11):7065—7067. [3]KIMH ,GRISHINAM ,RAOKV ,etal.Ce substitutedYIGfilmsgrownbypulsedlaserdepositionformagneto opticwaveguidedevices[J].IEEETransMagn,1999,35(5):3163—3165. [4]IBRAHIMNB ,EDWARDSC ,PALMERSB .PulsedlaserablationdepositionofyttriumirongarnetandceriumsubstitutedYIGfilms[J].JMagnMagnMater,2000,220:183—194. [5]KURODACS ,TANIYAMAT ,KITAMOTOY ,etal.Improvementinmagneto opticalpropertiesofBiYIGparticulatefilmsbyreductioninparticlesize[J].IEEETransMagn,2001,37(4):2432—2434. [6]KAWAIN ,KOMMOE ,NMIKAWAT ,etal.PreparationofBiYIGparticlesfordisplaydevices[J].IEEETransMagn,1994,30(6):4446—4448. [7]都有为.铁氧体[M].南京:江苏科技出版社,1995.DUYouwei.Ferrites(inChinese).Nanjing:JiangshuScientificandTechnologicPress,1995. [8]祝琳华,廖学品,郎小川,等.共沉淀法合成磷酸盐陶瓷Ca1-xBaxZr4P6O24粉体的研究[J].硅酸盐学报,2001,29(3):271—274.ZHULinhua,LIAOXuepin,LANGXiaochuan,etal.JChinCeramSoc(inChinese),2001,29(3):271—274. [9]张若华.稀土元素化学[M].天津:天津科技出版社,1985.ZHANGRuohua.ChemistryofRareEarthElements(inChinese).Tianjing:TianjingScientificandTechnologicPress,1985. [10]黄伯龄.矿物差热分析鉴定手册[M].北京:科学出版社,1987.HUANGBoling.DTAAnalyticalManuforMinerals(inChinese).Beijing:SciencePress,1987. [11]王宏志,高　濂,HIROKAZUKawaoka,等.多晶YAG陶瓷的制备及力学性能[J].硅酸盐学报,2001,29(1):35—38.WANGHongzhi,GAOLian,HIROKAZUKawaoka,etal.JChinCe ramSoc(inChinese),2001,.29(1):35—38. [12]PARKMB ,CHONH .Structuralandmagneticcharacteristicsofyttri umirongarnet(YIG ,Ce:YIG)filmspreparedbyRFmagnetronsput tertechniques[J].JMagnMagnMater,2001,231:253—264. [13]黄永杰,李世,兰中文.磁性材料[M].北京电子工业出版社,1995.HUANGYongjie,LIShifang,LANZhongwen.MagneticMaterials(inChinese).Beijing:ElectronicsIndustryPress,1995.

服务与反馈：

【文章下载】【加入收藏】