CuO掺杂对NaNbO_3–BaTiO_3无铅压电陶瓷性能的影响

作者：朱孔军谢实晖裘进浩柏林季宏丽

分类号：TM282

出版年,卷(期):页码：2010,38(6):1031-1035

DOI：

摘要：

利用传统烧结法制备CuO掺杂NaNbO3–BaTiO3无铅压电陶瓷,研究不同CuO掺量(0、0.1%、0.2%、0.3%、0.4%、1.0%和2.0%,摩尔分数)对样品显微结构、物相组成及电性能的影响。结果表明:CuO掺量对物相组成、压电性能、铁电性能及介电性能都有显著影响。当CuO掺量从0增大到0.3%时,压电性能增高;当CuO掺量超过0.3%时,压电性能明显下降。当CuO掺量为0.3%时,样品的综合性能最佳:压电常数(d33)为150pC/N,介电损耗(tanδ)为0.0174,机电耦合系数(kp)为30.19%,剩余极化强度(Pr)为13.5μC/cm2,矫顽场(Ec)为1.94kV/mm。

Lead-free NaNbO3 (NN)–BaTiO3 (BT) piezoelectric ceramics were prepared by the traditional sintering method. The ef-fects of different CuO contents (0,0.1%,0.2%,0.3%,0.4%,1.0%,and 2.0% in mole) on microstructure,phase composition and elec-tric properties of obtained samples were studied. The results show that the phase composition,piezoelectric,dielectric and ferroelec-tric properties of the lead-free ceramics are much influenced by the contents of doped CuO. The piezoelectric properties are enhanced when CuO content increases from 0 to 0.3%,and decrease when CuO content is more than 0.3%. When CuO content is 0.3%,the highest electric properties of piezoelectric constant d33 = 150 pC/N,dielectric loss tan δ = 0.017 4,planar coupling factor kp = 30.19%,remanent polarization Pr = 13.5 μC/cm2,and coercive electric field Ec = 1.94 kV/ mm are achieved,respectively.

基金项目：

国家自然科学基金(50872053);; 教育部重大项目培育基金(707031)资助项目

作者简介：

参考文献：

[1]IVANO I,DINO A,ARIANNA M,et al.Modeling and experimental validation of a piezoelectric micropump with novel no-moving-part valves[J].Sensors Actuators A.2007,133:128–140. [2]张建辉,黎毅力,刘菊银,等.“Y”型流管无阀压电泵的模拟与试验[J].光学精密工程,2008,16(4):669–677.ZHANG J H,LI Y L,LIU J Y,et al.Opt Precision Eng(in Chinese),2008,16(4):669–677. [3]阚君武,杨志刚,程光明,等.压电泵的现状与发展[J].光学精密工程,2002,10(6):619–625.KAN J W,YANG ZH G,CHEN G M.Opt Precision Eng(in Chinese),2002,10(6):619–625. [4]刘俊,秦岚,刘京城,等.一种新型差动式压电加速度传感器[J].光学精密工程,2007,15(6):903–907.LIU J,QIN L,LIU J C,et al.Opt Precision Eng(in Chinese),2007,15(6):903–907. [5]SAITO Y,TAKAO H,TANI T,et al.Lead-free piezoceramics[J].Nature,2004,432:84–87. [6]LI J F,WANG K,ZHANG B P,et al.Ferroelectric and piezoelectric properties of fine-grained Na0.5K0.5NbO3lead-free piezoelectric ce-ramics prepared by spark plasma sintering[J].J Am Ceram Soc,2006,89(2):706–709. [7]MATSUBARA,M,YAMAGUCHI,T,KIKUTA,K,et al.Sinterability and piezoelectric properties of(K,Na)NbO3ceramics with novel sin-tering aid[J].Jpn J Appl Phys1,2004,43(10):7159–7163. [8]XIE S H,ZHU K J,QIU J H,et al.Microstructure and electrical properties of NaNbO3–BaTiO3lead-free piezoelectric ceramics[J].Frontiers Mechan Eng in China,2009,4(3):345–349. [9]SAITO Y.Microstructural evolution of crystalline-oriented(K0.5Na0.5)NbO3piezoelectric ceramics with a sintering aid of CuO[J].J Am Ce-ram Soc,2006,89(6):1951–1956. [10]PARK J H,PARK J G,KIM B K.Effect of MnO2addition on the piezoelectric properties in Pb(Mg1/3Nb2/3)O3relaxor ferroelectrics[J].Mater Res Bull,2002,37:305–311. [11]YOO J H,HONG J I,SUH S.Effect of MnO2impurity on the modified PbTiO3system ceramics for power supply[J].Sensors Actuators,1999,78:168–171. [12]张凤鸣.陶瓷添加剂MnO2、Fe2O3、Li2CO3的热分析[J].压电与声光,1998,20(5):358–360.ZHANG Fengming.Piezoelectr Acoustooptics(in Chinese),1998,20(5):358–360. [13]PARK S H,AHN C W.Microstructure and piezoelectric properties of ZnO-added(Na0.5K0.5)NbO3ceramics[J].Jpn J Appl Phys,2004,43(8B):1072–1074. [14]AHN C W,SONG H C.Effect of MnO2on the piezoelectric properties of(1–x)(Na0.5K0.5)NbO3–xBaTiO3ceramics[J].Jpn J Appl Phys,2005,44(44):1361–1364. [15]HOU Y D,ZHU M K,GAO F,et al.Effect of MnO2Addition on the structure and electrical properties of Pb(Zn1/3Nb2/3)0.20(Zr0.50Ti0.50)0.80O3ceramics[J].J Am Ceram Soc,2004,87:847–850. [16]MATSUBARA M,YAMAGUCHI T.Synthesis and characterization of(Na0.5K0.5)(Nb0.7Ta0.3)O3piezoelectric ceramics sintered with sintering aid K5.4Cu1.3Ta10O29[J].Jpn J Appl Phys,2005,44(9):6618–6623. [17]JIAO G C,FAN H Q.Structure and piezoelectric properties of Cu-doped potassium sodium tantalite niobate ceramics[J].Mater Lett,2007,61:4185–4187.

服务与反馈：

【文章下载】【加入收藏】