热处理对不加热ITO/玻璃基底上沉积的PLZT铁电薄膜结构转变的影响
作者:蒋生蕊 王君 魏智强 
单位:兰州大学物理系 兰州大学物理系 兰州大学物理系 兰州730000  兰州730000  兰州730000 
关键词:锆钛酸铅镧铁电薄膜  结构转变  热处理 
分类号:TN304.9
出版年,卷(期):页码:2002,30(1):30-35
DOI:
摘要:
采用射频磁控溅射技术在不加热ITO/玻璃衬底上制备了PLZT( 9/ 5 2 / 48)铁电薄膜 .X射线衍射分析表明溅射气氛中φ(O2 )∶φ(Ar)为 3∶7的膜在PbO保护下 ,6 2 5℃热处理 15 0min后完全形成钙钛矿相的PLZT ,不存在第 2相 ,介电常数ε为 12 2 4.XPS表面成分分析及深度分析表明 :PbO保护气氛中热处理不仅可以防止失铅 ,而且还可以弥补在制膜过程中失去的铅 .用改进的Sawyer -Tower电路测量了薄膜的电滞回线 ,并获得剩余极化强度为 17.7μC/cm2 、矫顽场为 2 4.3kV/cm
my wife cheated on me now what website husband cheat
Ferroelectrics PLZT(9/52/48) thin films were deposited by RF magnetron sputtering on unheated ITO/glass substrates using an oxide sintered target with excess PbO. X_ray diffraction indicates that the PLZT thin films are completely structured by perovskite phase under the conditions of thermal annealing at 625 ℃ for 150 min in the sputtering gas of PbO with 30 percent oxygen in volume. The dielectric constant ( ε ) of the films is 1 224. XPS surface composition and depth analysis indicate that thermal annealing under the PbO protection not only avoid the Pb_loss phenomenon, but also compensates the lost lead in the processing of the deposition. Hysteresis loop was measured using a modified Sawyer-Tower circuit at room temperature. The remanent polarization and the coercive field are 17.7 μC/cm 2 and 24.3 kV/cm, respectively.
sumatriptan side effects sumatriptan side effects sumatriptan side effects
cialis discount coupons coupons for cialis 2016 cialis 2015 coupon
基金项目:
甘肃省自然科学基金资助项目 (ZR -97-0 6 1)
作者简介:
how do i know if my wife has cheated dating for married men read
redirect why do women cheat on their husbands unfaithful husband
how to catch a cheater link go
my husband cheated on me click here women who cheat on husband
参考文献:
[1] ChoiHW ,ParkYS ,DoughertyJ,etal.ElectricalandopticalpropertiesofPLZTthinfilmsonITOcoatedglassbysol-gelpro cessing[J].JMaterSci,2000,35(6):1475—1479. [2] HiranoT ,KawaiH ,SuzukiH ,etal.Lowtemperatureprocessingofsol-gelderivedPLZTthinfilm[J].Ferroelectrics,1999,231(1—4):799—804. [3] TunaboyluB ,HarveyP ,EsenerSC .Characterizationofdielectricandelectro_opticpropertiesofPLZT 9/65/35filmsonsapphireforelectro_opticapplications[J].IEEETUltrasonFerr,1998,45(4):1105—1112. [4] LuDX ,PunEYB ,WongEMW ,etal.RFsputteredPLZTthinfilmonPt/Tielectrode[J].IEEETUltrasonFerr,1997,44(3):675—680. [5] GomesMJM ,GomesED ,MantasPLQ ,etal.Growthandchar acterizationofPLZTfilms[J].ApplSurfSci,1996,96(8):779—783. [6] NakasimaH ,HazumiS ,KamiyaT ,etal.Electricalpropertiesforcapacitorsofdynamicrandomaccessmemoryon(Pb,La)·(Zr,Ti)O3thinfilmsbymetalorganicchemicalvapordeposition[J].JpnJApplPhyspart1,1994,33(9B):5139—5142. [7] LiuKS ,TsengTF ,LinIN .Improvementof(Pb1-xLax)·(ZryTi1-y)1-x/4O3ferroelectricthinfilmsbyuseofSrRuO3/Ru/Pt/Tibottomelectrodes[J].ApplPhysLett,1998,72(10):1182—1184. [8] GomesMJM .OnthepreparationofPLZTthinfilmsgrownbypulsedlaserdeposition[J].Vacuum,1999,52(1-2):61—66. [9] LinWJ,TsengTY ,WuYZ ,etal.GrowthandfatiguepropertiesofpulsedlaserdepositedPb1-xLax(ZryTiz)O3thinfilmswith[001]preferredorientation[J].JMaterSciMaterMed,1996,7(6):409—417. [10] JiangShenrui,PengDongliang,LiBin,etal.TheeffectofheattreatmentontheelectricalandopticalpropertiesoftransparentandconductiveCdIn2O4films[J].VacuumSciTechnol,1993,13(2):124—129. [11] PengDongliang,JiangShenrui.Investigationonthephysicalproper tiesanddefectsofCd2SnO4filmsdepositedbyRFreactivesputtering[J].ActaPhysSinica,1992,41(12):2055—2060. [12] PHI 5300InstrumentManual.USA :Perkin-ElmerCorpora_tion,1988.519—559
married cheaters cheat on my wife click
online women that cheat with married men married woman looking to cheat
redirect i dreamed my wife cheated on me unfaithful husband
why do wife cheat on husband why men cheat how to cheat wife
my wife cheated on me now what website husband cheat
abortion las vegas abortion pill online abortion pictures
服务与反馈:
文章下载】【加入收藏
中国硅酸盐学会《硅酸盐学报》编辑室
京ICP备10016537号-2
京公网安备 11010802024188号
地址:北京市海淀区三里河路11号    邮政编码:100831
电话:010-57811253  57811254    
E-mail:jccs@ceramsoc.com