硅酸盐学报

氯盐环境对PVA纤维增强水泥基复合材料抗冻性的影响

作者：张菊1 刘曙光1 闫长旺1 白建文1 闫敏2

单位：1. 内蒙古工业大学矿业学院呼和浩特 010051 2. 鄂尔多斯市质量监督站内蒙古鄂尔多斯 017000

分类号：TU528.581

出版年,卷(期):页码：2013,41(6):766-771

DOI：

摘要：

在氯盐环境和淡水环境中进行聚乙烯醇纤维增强水泥基复合材料(polyvinyl alcohol fiber reinforced engineered cementitious composite，PVA-ECC)快速冻融试验，研究了氯盐环境对试件外观形貌、质量损失率、相对动弹性模量和耐久性指数的影响。结果表明：氯盐环境中，PVA-ECC试件质量在冻融循环初期呈增大趋势，在冻融循环后期因表层严重剥落，导致质量下降，质量损失率显著增大，整个冻融循环过程中试件的耐久性指数较小，相对动弹性模量明显下降；淡水环境中PVA-ECC试件经历冻融循环后基本保持原有形状和尺寸，质量损失率变化幅度较小，相对动弹性模量下降趋势平缓，耐久性指数较大。与淡水环境相比，氯盐环境中PVA-ECC试件的抗冻性显著下降，表明氯盐环境对PVA-ECC抗冻性有重要影响。

The frost resistance of polyvinyl alcohol fiber reinforced engineered cementitious composite (PVA-ECC) in chloride and freshwater environments was investigated via an accelerated freeze-thaw test. Influence of chloride environment on the appearance morphology, mass loss ratio, relative dynamic elastic modulus (Erd) and durability indices was analyzed. The results show that the mass of specimen in chloride environment increases during first freeze-thaw cycles, but the mass and Erd both decrease, the mass loss rate increases during later freeze-thaw cycles because the surface layer of specimen flakes away seriously. The durability indices of specimen in chloride environment are less during whole freeze-thaw cycles. However, the original shape and size unchange, the mass loss rate changes slightly, Erd decreases and the durability indices are more for the specimen in freshwater environment during the freeze-thaw cycles. The frost resistance of specimen can decrease readily in chloride environment rather than in freshwater environment, illustrating that the chloride environment has a significant effect on the frost resistance of PVA-ECC.

基金项目：

国家自然科学基金(50968011，51168033)；内蒙古自然科学基金(2012MS0706)；内蒙古自治区高等学校科学研究项目(NJZY12058)及内蒙古工业大学科学研究项目(No.ZS201137)资助。

作者简介：

第一作者：张菊(1977—)，女，硕士，副教授。通信作者：刘曙光(1960—)，男，硕士，教授。

参考文献：

[1] 徐世烺, 蔡向荣. 超高韧性纤维增强水泥基复合材料基本力学性能[J]. 水利学报, 2009, 40(9): 1055–1063.
XU Shilang, CAI Xiangrong. J Hydraul Eng (in Chinese), 2009, 40(9): 1055–1063.
[2] LI V C, LEUNG C K Y. Steady-state and multiple cracking of short random fiber composites [J]. J Eng Mech, 1992, 118(11): 2246–2264.
[3] XU B, TOUTANJI H, GILBERT J. Impact resistance of poly (vinyl alcohol) fiber reinforced high-performance organic aggregate cementitious material [J]. Cem Concr Res, 2010, 40(2): 347–351.
[4] ?AHMARAN M, ÖZBAY E, YÜCEL H. Effect of fly ash and PVA fiber on microstructural damage and residual properties of engineered cementitious composites exposed to high temperatures [J]. J Mater Civ Eng, 2011, 23(12): 1735–1745.
[5] YUN H D, ROKUGO K. Freeze-thaw influence on the flexural properties of ductile fiber-reinforced cementitious composites (DFRCCs) for durable infrastructures [J]. Cold Reg Sci Technol, 2012, 78: 82–88.
[6] ÇAVDAR A. A study on the effects of high temperature on mechanical properties of fiber reinforced cementitious composites [J]. Composi Part B: Eng, 2012, 43(5): 2452–2463.
[7] 徐世烺, 蔡新华, 李贺东. 超高韧性水泥基复合材料抗冻耐久性能试验研究[J]. 土木工程学报, 2009, 42(9): 42–46.
XU Shilang, CAI Xinhua, LI Hedong. China Civ Eng J (in Chinese), 2009, 42(9): 42–46.
[8] 徐世烺, 蔡新华. 超高韧性水泥基复合材料碳化与渗透性能试验研究[J]. 复合材料学报, 2010, 27(3): 177–183.
XU Shilang, CAI Xinhua. Acta Mater Compos Sin (in Chinese), 2010, 27(3): 177–183.
[9] 王阵地, 姚燕, 王玲. 冻融循环与氯盐侵蚀作用下混凝土变形和损伤分析[J]. 硅酸盐学报, 2012, 40(8): 1133–1138.
WANG Zhendi, YAO Yan, WANG Ling. J Chin Ceram Soc, 2012, 40(8): 1133–1138.
[10] 施锦杰, 孙伟. 弯曲荷载与氯盐耦合作用下混凝土中钢筋锈蚀程度评估[J]. 硅酸盐学报, 2010, 38(7): 1201–1208.
SHI Jinjie, SUN Wei. J Chin Ceram Soc, 2010, 38(7): 1201–1208.
[11] 韩冰, 曹健, 董敬勋. 持续荷载作用对粉煤灰混凝土冻融性能的影响[J]. 中国铁道科学, 2012, 33(2): 33–37.
HAN Bing, CAO Jian, DONG Jingxun. China Railw Sci (in Chinese), 2012, 33(2): 33–37.
[12] 余红发, 孙伟, 李美丹. 荷载对混凝土在腐蚀–冻融作用下强度的影响[J]. 哈尔滨工业大学学报, 2010, 42(2): 297–301.
YU Hongfa, SUN Wei, LI Meidan. J Harbin Inst Technol (in Chinese), 2010, 42(2): 297–301.
[13] 慕儒, 缪昌文, 刘加平, 等. 氯化钠、硫酸钠溶液对混凝土抗冻性的影响及其机理[J]. 硅酸盐学报, 2001, 29(6): 523–528.
MU Ru, MIAO Changwen, LIU Jiaping, et al. J Chin Ceram Soc, 2001, 29(6): 523–528.
[14] BROWN P, BOTHE J J. The system CaO–Al2O3–CaCl2–H2O at 23 ± 2 ℃ and the mechanisms of chloride binding in concrete [J]. Cem Concr Res, 2004, 34(9): 1549–1553.

服务与反馈：

【文章下载】【加入收藏】