锆钛酸铅钡锶压电陶瓷的偏压特性

单位：1. 昆山攀特电陶科技有限公司江苏昆山 215300 2. 江苏大学材料科学与工程学院江苏镇江 212013

分类号：TM282

出版年,卷(期):页码：2014,42(8):00-00

DOI：

摘要：

采用扎膜工艺和固相反应法制备了(Pb0.70Ba0.26Sr0.04)(Zr0.52 Ti0.48)O3（PBSZT）压电陶瓷。通过扫描电镜和X射线衍射表征PBSZT陶瓷的结构和物相组成，用电容介损测试仪表征压电陶瓷的介质性能与激励场强，通过自建电路集成直流电源、标准电容，在低频频率特性测试仪上得到偏场强度对压电陶瓷介电性能的影响关系。结果表明：压电陶瓷材料的介电性能随着加载的电场强度的增大先逐渐升高，而后出现拐点开始降低；在偏压电场中，自由电容CT随正向偏场强度的增加逐渐减小，但随着反向偏场强度的增加逐渐增大。tan δ则随着正、反偏场强度的增加均呈现上升；压电陶瓷的机电耦合系数与偏场强度的关系，以零点为界，随着负偏场增强，Kp略显下降，反之，随正偏场增强，Kp缓慢增大。因此，压电陶瓷应用时应避开强场损耗高点；并在环境中施加正向偏场，有助于抑制压电陶瓷性能衰减。

(Pb0.70Ba0.26Sr0.04)(Zr0.52 Ti0.48)O3（PBSZT）piezo ceramics were prepared via the roll formation and solid-state reaction process. The microstructure and phase compositions of the ceramics were investigated by scanning electron microscopy and X-ray diffraction as well. The relationships among dielectric properties (CT, tanδ) and electric field strength，electromechanical coupling coefficient and bias field strength were investigated. The results show that the CT and tanδ firstly increase and then decrease dramatically with increasing the electric field strength, In the bias field, the CT decreases with increasing the positive bias field strength, and increases with increasing the negative bias field strength. The tanδ increases in both the positive bias field and the negative bias field. The Kp increases with increasing the positive bias field strength and varies in the same trend with decreasing the negative bias field strength. I is important to avoid the high loss point, and it is appropriate to restrain the attenuation of the piezo capability and provide a positive bias field on piezo ceramics applications.

基金项目：

作者简介：

通信作者：范景波(1985—)，男，硕士，工程师。

参考文献：

[1] YU Z, CHEN A, GUO R. et al. Dielectric properties and high tunability of Ba(Ti0.7Zr0.3)O3 ceramics under dc electric field[J]. Appl Phys Lett, 2002,81(7):1285-1287.
[2] SAWYER C B, TOWER C H. Rochelle salt as a dielectric[J]. Phys Rev,1930,35:269-275.
[3] 伍建新, 庄志强. PBLZT弛豫铁电陶瓷的动态及偏压介电和压电特性[J]. 无机材料学报，2000,15:97-102.
WU Jianxin, ZHUANG Zhiqiang. Dielectric and Piezoelectric Characteristics at Dynamic and DC Bias State for PBLZT Relaxor Ferroelectric Ceramic[J]. J Inorg Mater, 2000,15:97-102.
[4] YANG G., REN W, LIU S F. et al. Effects of Uniaxial Stress and DC Bias Field on the Piezoelectric, Dielectric, and Elastic Properties of Piezoelectric Ceramics[J]. 2000IEEE ULTRASONICS SYMPOSIUM,1005-1008.
[5] WANG Q M, ZHANG T, CHEN Q M, et al. Effect of DC bias field on the complex materias coefficients of piezoelectric resonators[J]. Sensors and Actuators A, 2003,109:149-155.
[6] HWANG H. J, YASUOKA M, SANDO M. et al. Fabrication, Sinterability, and Mechanical Properties of Lead Zirconate Titanate/Silver Composites[J]. J Am Ceram Soc, 1999,82(9):2417-2422.
[7] CHAISAN W, YIMNIRUN, ANANTA S. et al. Dielectric and ferroelectric properties of lead zirconate titanate-barium titanate ceramics prepared by a modified mixed-oxide method[J]. Mater Chem Phys,2007,104:113-118.
[8] LIU S F , PARK S E, SHROUT T R. et al. Electric field dependence of piezoelectric properties for rhombohedral 0.955Pb(Zn1/3Nb2/3)O3-0.045PbTiO3 single crystals [J]. J Appl Phys, 1999,85:2810-2814.
[9] 凌志远, 熊茂人, 陈楷. 压电陶瓷的极化反转过程[J]. 功能材料，1998, 29(5):530-533.
LING Zhiyuan, XIONG Maoren, CHEN Kai.. J Funct Mater, 1998, 29(5):530-533.
[10] OH KY, SAITO Y, FURUTA A, et al. Piezoelectricity in the Field-induced Ferroelectric Phase of Lead Zirconate-Based Antiferroelectrics[J]. J Am Ceram Soc, 1992,75(4):795-799.
[11] YAMASHIITA Y, YOSHIDA S, TAKAHASHI T. Effects of MnO Additive on Piezoelectric Properties in Modified (Pb, Ca)TiO3 Ferroelectric Ceramics[J]. J Appl Phys,1983,22: 40-42.

服务与反馈：

【文章下载】【加入收藏】