硅酸盐学报

沉管隧道壁中热-水-离子传输过程

作者：庞晓贇李乐桂强李克非

分类号：TU528

出版年,卷(期):页码：2015,43(2):2-3

DOI：10.14062/j.issn.0454-5648.2015.02.03

摘要：

考虑我国东南沿海在建的沉管隧道环境，针对沉管隧道壁所处的特殊环境条件建立了热-水-离子耦合传输模型，研究多离子多场作用下侵蚀性离子在沉管壁混凝土中的迁移过程。利用该传输模型计算了120年使用期内在不同温度和压力工况下的水分与离子分布。结果表明：隧道壁的水分迁移为内侧干燥过程与外侧海水渗入过程的叠加；温度变化对离子和水分传输的影响比外部水压变化更加显著；120年隧道外侧溶蚀深度有限，钢筋锈蚀诱发区域深度约为0.65 m，但锈蚀电流低于0.1 μA/cm2。

The multi-species transport of ions in sea-water in the concrete wall of immerged tube tunnels was investigated. Concrete immerged tunnels have a long designed life, which are exposed externally to sea-water and internally to traffic air. This particular exposure condition has an important impact on the long-term durability. A thermo-hydro-ionic (THI) model for the ions transport through the tunnel wall that concerns the mass, heat and electrical charge conservations was proposed. The THI model was applied to an ongoing project of immerged tube tunnel on the south-eastern coast of China for a designed life of 120 years for different working cases. The simulated results show that the moisture transport is superimposed by internal drying and external sea-water penetration. The temperature gradient has an more significant effect on the transport processes, compared to the external hydraulic pressure. The external leaching depth is small, the corrosion initiation range attains 0.65 m and the corrosion current is < 0.1 μA/cm2.

基金项目：

基金项目：国家科技支撑计划项目(2011BAG07B04).

作者简介：

第一作者：庞晓贇(1988—)，男，博士研究生。通信作者：李克非(1972—)，男，博士，教授。

参考文献：

参考文献:

[1] 王梦恕. 水下交通隧道发展现状与技术难题——兼论“台湾海峡海底铁路隧道建设方案”[J]. 岩石力学与工程学报, 2008, 27(11): 2163–2172.

WANG Mengshu. Chin J Rock Mech Eng, 2008, 27(11): 2163–2172.

[2] Rasmussen N S, Grantz W. Catalogue of immersed tunnels [J]. Tunn Underg Sp Tech, 1997, 12: 163–316.

[3] Glerum A. Developments in immersed tunnelling in Holland [J]. Tunn Underg Sp Tech, 1995, 10: 455–462.

[4] JOHannesson B, Yamada K, NILSSON L O. Multi-species ionic diffusion in concrete with account to interaction between ions in the pore solution and the cement hydrates [J]. Mater Struct, 2007, 40: 651–665.

[5] Mehta P K. Durability of concrete in marine environment-A review[J]. J Am Concr Institute, 1980, 65: 1–20.

[6] 常钧，房延凤，李勇. 钙硅比对水化硅酸钙加速碳化的影响[J]. 硅酸盐学报, 2014, 42(11): 1377–1382.

CHANG Jun, FANG Yanfeng, LI Yong. J Chin Ceram Soc, 2014, 42(11): 1377–1382.

[7] 施锦杰，孙伟. 混凝土中钢筋锈蚀研究现状与热点问题分析[J]. 硅酸盐学报, 2010, 38(9): 1753–1764.

SHI Jinjie, SUN Wei. J Chin Ceram Soc, 2010, 38(9): 1754–1764.

[8] Melchers R E, Li C Q. Reinforcement corrosion in concrete exposed to the North sea for more than 60 years [J]. Corrosion, 2009, 65: 554–566.

[9] Chen J K, Jiang M Q, Zhu J.Damage evolution in cement mortar due to erosion of sulphate [J]. Corros Sci, 2008, 50: 2478–2483.

[10] Vedalakshmi R, Saraswathy V, Yong A K. Performance evaluation of blended cement concretes under MgSO4 attack [J]. Mag Concr Res, 2011, 63: 669–681.

[11] Haga K, Sutou S,？？ et al. Effect of porosity on leaching of Ca from hardened ordinary Portland cement paste [J]. Cem Concr Res, 2005, 35: 1764–1775.

[12] 曲立清, 金祖权, 赵铁军, 等. 海底隧道钢筋混凝土基于氯盐腐蚀的耐久性参数设计研究 [J]. 岩石力学与工程学报, 2007, 26(11): 2333–2340.

QU Liqing, JIN Zuquan, Zhao Tiejun, et al. Chin J Rock Mech Eng, 2007, 26(11): 2333–2340.

[13] Fabbri A, Coussy O, FEN-CHONG T, et al. Are deicing salts necessary to promote scaling in concrete? [J]. J Eng Mech-ASCE, 2008, 134(7): 589–598.

[14] DE VRIES D A, Kruger A J. On the value of the diffusion coefficient of water vapor in air. Proceedings of Colloque International du CNRS 160: Phénomènes de Transport avec Changement de Phase dans les Milieux Poreux ou Collo?daux [C]. CNRS, 1966: 61-72.

[15] Van-Genuchenten M T. A closed-form equation for prediction the hydraulic conductivity of unsaturated soil [J]. Soil Sci Soc Am J, 1980, 44: 892–898.

[16] Zeng Q, Wang Y, Li K. Uniform Model for Moisture Transport in Porous Materials and Its Application to Concrete at Selected Chinese Regions [J]. J Mater Civ Eng-ASCE, 26(6).

[17] Tang L, Nilsson L-O. Chloride binding capacity and binding isotherms of OPC pastes and mortars [J]. Cem Concr Res, 1993, 23(2): 247–253.

[18] Yokozeki K, Watanabe K, SAKATA N, et al. Modeling of leaching from cementitious materials used in underground environment [J]. Appl Clay Sci, 2004, 26: 293–308.

[19] Saetta A V, Scotta R V. Analysis of chloride diffusion into partially saturated concrete [J]. ACI Mater J, 1993, 5: 441–451.

[20] Shen J Y, Dangla P, Thiery M. Reactive transport modeling of CO2 through cementitious materials under CO2 geological storage conditions [J]. Int J Greenh Gas Con, 2013, 18: 75–87.

[21] Dangla P, Dridi W. Rebar corrosion in carbonated concrete exposed to variable humidity conditions, Interpretation of Tuutti's curve [J]. Corros Sci, 2009, 51: 1747–1756.

[22] LOthenbach B, Winnefeild F. Thermodynamic modeling of the hydration of Portland cement [J]. Cem Concr Res, 2006, 36: 209–226.

[23] Lothenbach B, Matschei T, MOSCHNER G, et al. Thermodynamic modeling of the effect of temperature on the hydration and porosity of Portland cement [J]. Cem Concr Res, 2008, 38: 1–18.

[24] Dangla P. A modeling platform based on finite volume/element methods.2014, http://perso.lcpc.fr/dangla.patrick/bil.

[25] Katz A J, Thompson A H. Quantitative prediction of permeability in porous rock [J]. Phys Rev B, 1986, 34: 8179–8181.

[26] Ki Y A, Ha-Won S. Chloride threshold level for corrosion of steel in concrete [J]. Corros Sci, 2007, 49: 4113–4133.

[27] Yu B, Yang L F, WU M, et al. Practical model for predicting corrosion rate of steel reinforcement in concrete structures [J]. Constr Build Mater, 2014, 54: 385–401.

[28] Ghods P, Isgor O B, Pour-Ghaz M. Experimental verification and application of a practical corrosion model for uniformly depassivated steel in concrete [J]. Mater Struct, 2008, 41: 1211–1223.

[29] DuraCrete. Probabilistic performance based durability design of concrete structures: Modeling of degradation [R]. Contract BRPR- CT95-0132, Project BE95-1347, Document BE95-1347/R4-5. The Netherlands.

服务与反馈：

【文章下载】【加入收藏】