粉煤灰贝利特水泥的研究现状与前景
作者:方永浩 承礼清 龚泳帆 杨文娟 
单位:河海大学力学与材料学院 南京210098 
关键词:粉煤灰贝利特水泥 水热合成 低温烧成 强度 耐久性 
分类号:TQ172.1
出版年,卷(期):页码:2015,43(2):5-6
DOI:10.14062/j.issn.0454-5648.2015.02.06
摘要:

 介绍了3类高贝利特水泥的特点和活性贝利特的研究现状,重点介绍了粉煤灰贝利特水泥的原材料、制备方法、水热合成产物、熟料组成、水泥水化和物理力学性能及耐久性等方面的研究进展,分析了料块水热合成?煅烧法和料浆水热合成?煅烧法的差异、粉煤灰贝利特水泥研究开发中存在的问题与原因及发展前景,对粉煤灰贝利特水泥的进一步研究从有效的水热处理方法、合理的熟料煅烧温度制度、石膏种类与掺量、粉磨细度的优化、以及适宜缓凝剂和减水剂的开发和应用等几个方面提出了相关建议。

how to cheat read wife cheat story
why women cheat on husbands online link

 The characteristics of the three types of high belite cement were introduced. Recent development on active belite was reviewed. The detailed information on studies of fly ash belite cement, including raw materials, preparation processes, hydrothermal-synthesized products, mineral composition, hydration, physical and mechanical properties and durability were represented. The difference between block hydrothermal-calcination process and slurry hydrothermal-calcination process was comparatively discussed. The problems in the development of fly ash belite cement and the possible reasons, the prospect of developing and application of the cement were analyzed. Several aspects were proposed for further studies of fly ash belite cement.

married cheaters how many women cheat click
My wife cheated on me why wives cheat on husbands reasons married men cheat
cialis coupon cialis coupon cialis coupon
基金项目:
基金项目:国家自然科学基金(项目编号:51139001);江苏省产学研联合创新——前瞻性联合研究项目(BY2014002-04)资助。
作者简介:
第一作者:方永浩(1956-),男,博士,教授。
married cheaters cheat on my wife click
online read here open
read read here link
My wife cheated on me women cheat because reasons married men cheat
abortion pill abortion pill abortion pill
参考文献:

 参考文献:

[1] 中华人民共和国国家统计局. 中华人民共和国2013年国民经济和社会发展统计公报[J]. 中国统计, 2014(3): 6–14.
The National Bureau of Statistics of the People's Republic of China. Chin Stat (in Chinese), 2014(3): 6–14. 
[2] CHATTERJEE A K. High belite cements—present status and future. Technological options: Part I [J]. Cem Concr Res, 1996, 26(8): 1213–1225.
[3] 隋同波, 刘克忠, 王 晶, 等. 高贝利特水泥的性能研究[J]. 硅酸盐学报, 1999, 27(4): 488–492.
SUI Tongbo, LIU Kezhong, WANG Jing, et al. J Chin Ceram Soc, 1999, 27(4): 488–492.
[4] KACIMI L, SIMON-MASSERON A, SALEM S, et al. Synthesis of belite cement clinker of high hydraulic reactivity[J]. Cem Concr Res, 2009, 39(7): 559–565.
[5] CHEN Yingliang, LIN Chienjung, KO Mingsheng, et al. Characterization of mortars from belite-rich clinkers produced from inorganic wastes [J]. Cem Concr Compos, 2011, 33(2): 261–266.
[6] GLASSER P, ZHANG L. High-performance cement matrices based on calcium sulfoaluminate–belite compositions [J]. Cem Concr Res, 2001, 31(12): 1881–1886.
[7] QUILLIN K. Performance of belite–sulfoaluminate cements [J]. Cem Concr Res, 2001, 31(9):1341–1349.
[8] ?IVICA V. Properties of blended sulfoaluminate belite cement [J]. Constr Build Mater, 2000, 14(8): 433–437.
[9] 张卫伟, 芦令超, 常 钧, 等. 贝利特-硫铝酸钡钙水泥的制备技术与力学性能[J]. 硅酸盐通报, 2007, 26(2): 344–348, 400. 
ZHANG Weiwei, LU Lingchao, CHANG Jun, et al. Bull Chin Ceram Soc (in Chinese), 2007, 26(2): 344–348, 400.
[10] IACOBESCU R I, PONTIKES Y, KOUMPOURI D, et al. Synthesis, characterization and properties of calcium ferroaluminate belite cements produced with electric arc furnace steel slag as raw material [J]. Cem Concr Compos, 3013, 44(1): 1–8.
[11] MING Panrong, YANG Nanru, ZHONG Baiqian, et al. Special Low-Lime Fly Ash Cement [C]// Proc1985 Beijing Int Symp Cem Concr. Beijing: China Building Industry Press, 1985, Vol I: 444–455. 
[12] 杨南如. 以C2S为主要矿物组成的低碳水泥初探[J]. 水泥技术, 2010 (4): 20–25.
YANG Nanru. Cem Tech (in Chinese), 2010 (4): 20–25. 
[13] PIMRAKSA K, HANJITSUWAN S, CHINDAPRASIRT P. Synthesis of belite cement from lignite fly ash [J]. Ceram Int, 2009, 35(6): 2415–2425.
[14] KACIMI L, CYR M, CLASTRES P. Synthesis of α’L-C2S cement from fly-ash using the hydrothermal method at low temperature and atmospheric pressure [J]. J Hazard Mater, 2010, 181(1-3): 593–601.
[15] GUERRERO A, GOÑI S, MACÍAS A, et al. Mechanical properties, pore size distribution, and pore solution of fly ash-belite cement mortars[J]. Cem Concr Res, 1999, 29(11): 1753–1758.
[16] DELLA M. ROY D, OYEFESOBI S O.  Preparation of very reactive Ca2SiO4 powder[J]. J Am Ceram Soc, 1977, 60(3-4): 178–180.
[17] 杨南如, 钟白茜. 活性C2S的研究[J]. 硅酸盐学报, 1982, 10 (2): 161–166. 
YANG Nanru, ZHONG Baiqian. J Chin Ceram Soc, 1982, 10(2): 161–166. 
[18] 杨南如, 王占文, 钟白茜. 活性C2S的形成机理[J]. 硅酸盐学报, 1986, 14(4): 385–391. 
YANG Nanru, WANG Zhanwen, ZHONG Baiqian. J Chin Ceram Soc, 1986, 14(4): 385–391. 
[19] 钟白茜, 杨南如.活性C2S的水化[J]. 南京化工学院学报, 1987, 9(2): 63–72. 
ZHONG Baiqian, YANG Nanru. J Nanjing Univ Technol: Nat Sci (in Chinese), 1987, 9(2): 63–72. 
[20] YANG Nanru, ZHONG Baiqian, WANG Zhanwen. An active dicalcium silicate—Preparation and hydration[C]// Proc 8th Int Conf Chem Cem, Rio de Janeir: [s.n.], 1986: Vol III, 22–27. 
[21] 张华, 杨南如, 万玉金, 等. 高活性 C2S的正电子湮没研究 [J].硅酸盐学报, 1992, 20(4): 309–314. 
ZHANG Hua, YANG Nanru, WAN Yujin, et al. J Chin Ceram Soc,1992,20(4): 309–314. 
[22] YANG Nanru, ZHANG Hua, ZHONG Baiqian. Study on hydraulic reactivity and structural behaviour of very active dicalcium smcate[c]∥Proc 9th Int Conf Chem Cem, New Delhi: [s.n.],1992, Vol IV: 285–291. 
[23] 钟白茜, 杨南如, 冈田能彦. 用29Si-NMR和TMS-GC研究由水热合成CSH脱水形成C2S的过程[J]. 硅酸盐学报, 1994, 22(6): 566-572. 
ZHONG Baiqian, YANG Nanru, OKADA Y. J Chin Ceram Soc, 1994, 22(6): 566–572. 
[24] ISHIDA H, SASAKI K, OKADA Y, et al. Highly reative dicalcium silicate prepared from hillebrandite: C-S-H with Ca/Si=1.9 ~2.0[C]//Proc 9th Int Conf Chem Cem, New Delhi: [s.n.], 1992, Vol IV: 76–82. 
[25] ISHIDA H, KABUCHI K, SASAKI K, et al. Low temperature synthesis of β-Ca2SiO4 from hillebrandite [J]. J Am Ceram Soc, 1992, 75(9): 2427–2432. 
[26] ISHIDA H, YAMAZAKI S, SASAKI K, et al. α-dicalcium silicate hydrate: Preparation, decomposed phase, and its hydration[J]. J Am Ceram Soc, 1993, 76(7): 1707–1712. 
[27] OKADA Y, SASAKI K, ZHONG Baiqian, et al. Formation processes of β-C2S by the decomposition of hydrothermally prepared C-S-H with Ca(OH)2[J]. J Am Ceram Soc, 1994, 77(5): 1319–1323. 
[28] ISHIDA H, SASAKI K, MITUSDA T. Highly reactive β-dicalcium silicate(I): Hydration behavior at room temperature [J]. J Am Ceram Soc,1992,75(2): 353–358. 
[29] ISHIDA H, OKADA Y, M ITUSDA T. Highly reactive β-dicalcium silicate(II): Hydration behavior at 25℃ followed by 29Si nuclear magnetic resonance[J]. J Am Ceram Soc, 1992, 7(2): 359–363. 
[30] SASAKI K, ISHIDA H, OKADA Y, et al. Highly reactive β-dicalcium silicate(V): Influence of specific surface area on the hydration[J]. J Am Ceram Soc, 1993,73(4): 870–874. 
[31] OKASA Y, ISHIDA H, SASAKI J K, et al. Characterization of C-S-H from highly reactive β-dicalcium silicate prepared from hillebrandite[J]. J Am Ceram Soc, 1994, 77(5): 1313–1318.
[32] 杨南如. 水热合成β-C2S的研究进展[J]. 建筑材料学报, 2011, 14(2): 145-154.
YANG Nanru. J Build Mater, 2011, 14(2): 145–154.
[33] KURDOWSKI W, DUSZAK S, TRYBALSKA B. Belite produced by means of low-temperature synthesis[J]. Cem Concr Res, 1997, 27(1): 51–62.
[34] GEORGESCU M, TIPAN J, BADANOIU A, et al. Highly reactive dicalcium silicate synthesised by hydrothermal process [J]. Cem Concr Compos, 2000. 22(5): 315–319. 
[35] SINGH N B, RAI S, SINGH N. Highly reactive β-dicalcium silicate [J]. J Am Ceram Soc, 2002, 85(9): 2171–2176.
[36] SINGH N B. Hydrothermal synthesis of β-dicalcium silicate (β-Ca2SiO4) [J]. Prog Cryst Growth Charact Mater, 2006, 52(1-2): 77–83. 
[37] MAZOUZI W, KACIMI L, CYR M, et al. Properties of low temperature belite cements made from aluminosilicate wastes by hydrothermal method[J]. Cem Concr Comp, 2014, 53(4): 170–177.
[38] JIANG WM, ROY DM. Hydrothermal processing of new fly ash cement [J]. Ceram Bull, 1997,71(4): 642–647.
[39] GOÑI S, GUERRERO A, LUXÁN M P, et al. Activation of the fly ash pozzolanic reaction by hydrothermal conditions [J]. Cem Concr Res, 2003, 33(7): 1399–1405.
[40] GOÑI S, GUERRERO A, Luxán M P, et al. Dehydration of pozzolanic products hydrothermally synthesized from flyash: microstructure evolution [J]. Mater Res Bull, 2000, 35(8): 1333–1344
[41] GUERRERO A, GOÑI S, MACÍAS A, et al. Effect of the starting fly ash on the microstructure and mechanical properties of fly ash-belite cement mortars [J]. Cem Concr Res, 2000, 30(4): 553–559.
[42] GUERRERO A, GOÑI S, CAMPILLO I, et al. Belite cement clinker from coal fly ash of high Ca content. Optimization of synthesis parameters [J]. Environ Sci Technol 2004, 38(11): 3209–3213.
[43] GOÑI S, GUERRERO A. SEM/EDX characterization of the hydration products of belite cements from class C coal fly ash [J]. J Am Ceram Soc, 2007, 90(12): 3915–3922.
[44] GUERRERO A, GOÑI S, MACÍAS A, et al. Hydraulic activity and microstructural characterization of new fly ash-belite cements synthesized at different temperatures [J]. J Mater Res, 1999, 14(6): 2680–2687.
[45] GUERRERO A, GOÑI S, MORAGUES A, et al. Microstructure and mechanical performance of belite cements from high calcium coal fly ash [J]. J Am Ceram Soc. 2005, 88(7): 1845–1853.
[46] GOÑI S, GUERRERO A. Study of alkaline hydrothermal activation of belite cements by thermal analysis [J]. J Therm Anal Calorimetry, 2009, 99(2): 471–477.
[47] GUERRERO A, GOÑI S, DOLADO J S. Belite cements modifications of calcium silicate hydrate (C-S-H) gel by alkaline hydrothermal activation[J]. ACI Mater, 2009, 106(2): 138–143.
[48] GOÑI S, GUERRERO A. Hydraulic activity of belite cement from class C coal fly ash. Effect of curing and admixtures [J]. Mater Constr, 2006, 56(283): 61–77.
[49] GOÑI S, GUERRERO A. Modifications of the C-S-H gel by hydration at 40ºC of belite cements from coal fly ash Class C [J]. J Am Ceram Soc, 2008, 91 (1): 209–214.
[50] GUERRERO A, GOÑI S, ALLEGRO V R. Durability of class C fly ash belite cement in simulated sodium chloride radioactive liquid waste: Influence of temperature [J]. J Hazard Mater, 2009, 162(2-3): 1099–1102.
[51] GUERRERO A, GOÑI S, ALLEGRO V R. Resistance of class C fly ash belite cement to simulated sodium sulphate radioactive liquid waste attack [J]. J Hazard Mater, 2009, 161 (2-3): 1250–1254.
[52] GUERRERO A, GOÑI S, MACÍAS A, Durability of new fly ash-belite cement mortars in sulfated and chloride medium [J]. Cem Concr Res, 2000, 30 (8): 1231–1238.
[53] GUERRERO A, GOÑI S, ALLEGRO V R. Effect of temperature on the durability of class C fly ash belite cement in simulated radioactive liquid waste: Synergy of chloride and sulphate ions [J]. J Hazard Mater, 2009, 165 (1-3): 903–908.
[54] MCCARTHY M J, JONES M R, ZHENG L, et al. Characterising long-term wet-stored fly ash following carbon and particle size separation[J]. Fuel, 2013, 111: 430–441.
why women cheat on husbands online link
why do wife cheat on husband why wifes cheat how to cheat wife
why married men cheat on their wives women cheat on men
my wife cheated on me now what website husband cheat
doxycycline doxycycline doxycycline
cialis coupon cialis coupon cialis coupon
服务与反馈:
文章下载】【加入收藏
中国硅酸盐学会《硅酸盐学报》编辑室
京ICP备10016537号-2
京公网安备 11010802024188号
地址:北京市海淀区三里河路11号    邮政编码:100831
电话:010-57811253  57811254    
E-mail:jccs@ceramsoc.com