粉煤灰贝利特水泥的研究现状与前景
作者:方永浩 承礼清 龚泳帆 杨文娟 
单位:河海大学力学与材料学院 南京210098 
关键词:粉煤灰贝利特水泥 水热合成 低温烧成    耐久性 
分类号:TQ172.1
出版年,卷(期):页码:2015,43(2):165-173
DOI:10.14062/j.issn.0454-5648.2015.02.06
摘要:

 介绍了3类高贝利特水泥的特点和活性贝利特

 
的研究现状,重点介绍了粉煤灰贝利特水泥的原材料、
 
制备方法、水热合成产物、熟料组成、水泥水化和物理
 
力学性能及耐久性等方面的研究进展,分析了料块水热
 
合成–煅烧法和料浆水热合成–煅烧法的差异、粉煤灰
 
贝利特水泥研究开发中存在的问题与原因及发展前景,
 
对粉煤灰贝利特水泥的进一步研究从有效的水热处理方
 
法、合理的熟料煅烧温度制度、石膏种类与掺量、粉磨
 
细度的优化、以及适宜缓凝剂和减水剂的开发和应用等
 
几个方面提出了相关建议。
read cheat on husband signs of infidelity
why do wife cheat on husband why men cheat how to cheat wife
abortion las vegas abortion pill online abortion pictures
doxycycline doxycycline doxycycline

  The characteristics of the three 

 
types of high belite cement were introduced. 
 
Recent development on active belite was 
 
reviewed. The detailed information on studies 
 
of fly ash belite cement, including raw 
 
materials, preparation processes, 
 
hydrothermal-synthesized products, mineral 
 
composition, hydration, physical and 
 
mechanical properties and durability were 
 
represented. The difference between block 
 
hydrothermal-calcination process and slurry 
 
hydrothermal-calcination process was 
 
comparatively discussed. The problems in the 
 
development of fly ash belite cement and the 
 
possible reasons, the prospect of developing 
 
and application of the cement were analyzed. 
 
Several aspects were proposed for further 
 
studies of fly ash belite cement.
redirect how to cheat why women cheat on men they love
read percentage of women who cheat signs of infidelity
基金项目:
基金项目:国家自然科学基金(51139001);江苏省产学 研联合创新——前瞻性联合研究项目(BY2014002-04)资助。
作者简介:
第一作者:方永浩(1956-),男,博士,教授。
why do wife cheat on husband why wifes cheat how to cheat wife
cialis coupon cialis coupon cialis coupon
参考文献:

 参考文献:

[1] 中华人民共和国国家统计局. 中华人民共和国
 
2013年国民经济和社会发展统计公报[J]. 中国统计, 
 
2014(3): 6–14.
The National Bureau of Statistics of the 
 
People's Republic of China. Chin Stat (in 
 
Chinese), 2014(3): 6–14. 
[2] CHATTERJEE A K. High belite cements—
 
present status and future. Technological 
 
options: Part I [J]. Cem Concr Res, 1996, 26
 
(8): 1213–1225.
[3] 隋同波, 刘克忠, 王晶, 等. 高贝利特水泥
 
的性能研究[J]. 硅酸盐学报, 1999, 27(4): 488–
 
492.
SUI Tongbo, LIU Kezhong, WANG Jing, et al. J 
 
Chin Ceram Soc, 1999, 27(4): 488–492.
[4] KACIMI L, SIMON-MASSERON A, SALEM S, 
 
et al. Synthesis of belite cement clinker of 
 
high hydraulic reactivity[J]. Cem Concr Res, 
 
2009, 39(7): 559–565.
[5] CHEN Yingliang, LIN Chienjung, KO 
 
Mingsheng, et al. Characterization of mortars 
 
from belite-rich clinkers produced from 
 
inorganic wastes [J]. Cem Concr Compos, 2011, 
 
33(2): 261–266.
[6] GLASSER P, ZHANG L. High-performance 
 
cement matrices based on calcium 
 
sulfoaluminate–belite compositions [J]. Cem 
 
Concr Res, 2001, 31(12): 1881–1886.
[7] QUILLIN K. Performance of belite–
 
sulfoaluminate cements [J]. Cem Concr Res, 
 
2001, 31(9):1341–1349.
[8] ?IVICA V. Properties of blended 
 
sulfoaluminate belite cement [J]. Constr Build 
 
Mater, 2000, 14(8): 433–437.
[9] 张卫伟, 芦令超, 常钧, 等. 贝利特-硫铝酸
 
钡钙水泥的制备技术与力学性能[J]. 硅酸盐通报, 
 
2007, 26(2): 344–348, 400. 
ZHANG Weiwei, LU Lingchao, CHANG Jun, et al. 
 
Bull Chin Ceram Soc (in Chinese), 2007, 26(2): 
 
344–348, 400.
[10] IACOBESCU R I, PONTIKES Y, KOUMPOURI 
 
D, et al. Synthesis, characterization and 
 
properties of calcium ferroaluminate belite 
 
cements produced with electric arc furnace 
 
steel slag as raw material [J]. Cem Concr 
 
Compos, 3013, 44(1): 1–8.
[11] MING Panrong, YANG Nanru, ZHONG 
 
Baiqian, et al. Special Low-Lime Fly Ash 
 
Cement [C]// Proc1985 Beijing Int Symp Cem 
 
Concr. Beijing: China Building Industry Press, 
 
1985, Vol I: 444–455. 
[12] 杨南如. 以C2S为主要矿物组成的低碳水泥初
 
探[J]. 水泥技术, 2010 (4): 20–25.
YANG Nanru. Cem Tech (in Chinese), 2010 (4): 
 
20–25. 
[13] PIMRAKSA K, HANJITSUWAN S, 
 
CHINDAPRASIRT P. Synthesis of belite cement 
 
from lignite fly ash [J]. Ceram Int, 2009, 35
 
(6): 2415–2425.
[14] KACIMI L, CYR M, CLASTRES P. Synthesis 
 
of α’L-C2S cement from fly-ash using the 
 
hydrothermal method at low temperature and 
 
atmospheric pressure [J]. J Hazard Mater, 
 
2010, 181(1-3): 593–601.
[15] Guerrero A, Goñi S, Macías A, et al. 
 
Mechanical properties, pore size distribution, 
 
and pore solution of fly ash-belite cement 
 
mortars[J]. Cem Concr Res, 1999, 29(11): 1753
 
–1758.
[16] DELLA M. ROY D, OYEFESOBI S O.  
 
Preparation of very reactive Ca2SiO4 powder
 
[J]. J Am Ceram Soc, 1977, 60(3-4): 178–180.
[17] 杨南如, 钟白茜. 活性C2S的研究[J]. 硅酸
 
盐学报, 1982, 10 (2): 161–166. 
YANG Nanru, ZHONG Baiqian. J Chin Ceram Soc, 
 
1982, 10(2): 161–166. 
[18] 杨南如, 王占文, 钟白茜. 活性C2S的形成机
 
理[J]. 硅酸盐学报, 1986, 14(4): 385–391. 
YANG Nanru, WANG Zhanwen, ZHONG Baiqian. J 
 
Chin Ceram Soc, 1986, 14(4): 385–391. 
[19] 钟白茜, 杨南如.活性C2S的水化[J]. 南京化
 
工学院学报, 1987, 9(2): 63–72. 
ZHONG Baiqian, YANG Nanru. J Nanjing Univ 
 
Technol: Nat Sci (in Chinese), 1987, 9(2): 63
 
–72. 
[20] YANG Nanru, ZHONG Baiqian, WANG 
 
Zhanwen. An active dicalcium silicate—
 
Preparation and hydration[C]// Proc 8th Int 
 
Conf Chem Cem, Rio de Janeir: [s.n.], 1986: 
 
Vol III, 22–27. 
[21] 张华, 杨南如, 万玉金, 等. 高活性 C2S的
 
正电子湮没研究 [J].硅酸盐学报, 1992, 20(4): 309
 
–314. 
ZHANG Hua, YANG Nanru, WAN Yujin, et al. J 
 
Chin Ceram Soc,1992,20(4): 309–314. 
[22] YANG Nanru, ZHANG Hua, ZHONG Baiqian. 
 
Study on hydraulic reactivity and structural 
 
behaviour of very active dicalcium smcate[c]∥
 
Proc 9th Int Conf Chem Cem, New Delhi: 
 
[s.n.],1992, Vol IV: 285–291. 
[23] 钟白茜, 杨南如, 冈田能彦. 用29Si-NMR和
 
TMS-GC研究由水热合成CSH脱水形成C2S的过程[J]. 硅
 
酸盐学报, 1994, 22(6): 566-572. 
ZHONG Baiqian, YANG Nanru, OKADA Y. J Chin 
 
Ceram Soc, 1994, 22(6): 566–572. 
[24] ISHIDA H, SASAKI K, OKADA Y, et al. 
 
Highly reactive dicalcium silicate prepared 
 
from hillebrandite: C-S-H with Ca/Si=1.9 ~2.0
 
[C]//Proc 9th Int Conf Chem Cem, New Delhi: 
 
[s.n.], 1992, Vol IV: 76–82. 
[25] ISHIDA H, KABUCHI K, SASAKI K, et al. 
 
Low temperature synthesis of β-Ca2SiO4 from 
 
hillebrandite [J]. J Am Ceram Soc, 1992, 75
 
(9): 2427–2432. 
[26] ISHIDA H, YAMAZAKI S, SASAKI K, et al. 
 
α-dicalcium silicate hydrate: Preparation, 
 
decomposed phase, and its hydration[J]. J Am 
 
Ceram Soc, 1993, 76(7): 1707–1712. 
[27] OKADA Y, SASAKI K, ZHONG Baiqian, et 
 
al. Formation processes of β-C2S by the 
 
decomposition of hydrothermally prepared C-S-H 
 
with Ca(OH)2[J]. J Am Ceram Soc, 1994, 77(5): 
 
1319–1323. 
[28] ISHIDA H, SASAKI K, MITUSDA T. Highly 
 
reactive β-dicalcium silicate(I): Hydration 
 
behavior at room temperature [J]. J Am Ceram 
 
Soc,1992,75(2): 353–358. 
[29] ISHIDA H, OKADA Y, M ITUSDA T. Highly 
 
reactive β-dicalcium silicate(II): Hydration 
 
behavior at 25℃ followed by 29Si nuclear 
 
magnetic resonance[J]. J Am Ceram Soc, 1992, 
 
7(2): 359–363. 
[30] SASAKI K, ISHIDA H, OKADA Y, et al. 
 
Highly reactive β-dicalcium silicate(V): 
 
Influence of specific surface area on the 
 
hydration[J]. J Am Ceram Soc, 1993,73(4): 870
 
–874. 
[31] OKASA Y, ISHIDA H, SASAKI J K, et al. 
 
Characterization of C-S-H from highly reactive 
 
β-dicalcium silicate prepared from 
 
hillebrandite[J]. J Am Ceram Soc, 1994, 77(5): 
 
1313–1318.
[32] 杨南如. 水热合成β-C2S的研究进展[J]. 建
 
筑材料学报, 2011, 14(2): 145-154.
YANG Nanru. J Build Mater, 2011, 14(2): 145–
 
154.
[33] KURDOWSKI W, DUSZAK S, TRYBALSKA B. 
 
Belite produced by means of low-temperature 
 
synthesis[J]. Cem Concr Res, 1997, 27(1): 51–
 
62.
[34] GEORGESCU M, TIPAN J, BADANOIU A, et 
 
al. Highly reactive dicalcium silicate 
 
synthesised by hydrothermal process [J]. Cem 
 
Concr Compos, 2000. 22(5): 315–319. 
[35] SINGH N B, RAI S, SINGH N. Highly 
 
reactive β-dicalcium silicate [J]. J Am Ceram 
 
Soc, 2002, 85(9): 2171–2176.
[36] SINGH N B. Hydrothermal synthesis of 
 
β-dicalcium silicate (β-Ca2SiO4) [J]. Prog 
 
Cryst Growth Charact Mater, 2006, 52(1-2): 77
 
–83. 
[37] MAZOUZI W, KACIMI L, CYR M, et al. 
 
Properties of low temperature belite cements 
 
made from aluminosilicate wastes by 
 
hydrothermal method[J]. Cem Concr Comp, 2014, 
 
53(4): 170–177.
[38] JIANG WM, ROY DM. Hydrothermal 
 
processing of new fly ash cement [J]. Ceram 
 
Bull, 1997,71(4): 642–647.
[39] GOÑI S, GUERRERO A, Luxán M P, et al. 
 
Activation of the fly ash pozzolanic reaction 
 
by hydrothermal conditions [J]. Cem Concr Res, 
 
2003, 33(7): 1399–1405.
[40] GOÑI S, GUERRERO A, Luxán M P, et al. 
 
Dehydration of pozzolanic products 
 
hydrothermally synthesized from flyash: 
 
microstructure evolution [J]. Mater Res Bull, 
 
2000, 35(8): 1333–1344
[41] GUERRERO A, GOÑI S, MACÍAS A, et al. 
 
Effect of the starting fly ash on the 
 
microstructure and mechanical properties of 
 
fly ash-belite cement mortars [J]. Cem Concr 
 
Res, 2000, 30(4): 553–559.
[42] GUERRERO A, GOÑI S, CAMPILLO I, et al. 
 
Belite cement clinker from coal fly ash of 
 
high Ca content. Optimization of synthesis 
 
parameters [J]. Environ Sci Technol 2004, 38
 
(11): 3209–3213.
[43] GOÑI S, GUERRERO A. SEM/EDX 
 
characterization of the hydration products of 
 
belite cements from class C coal fly ash [J]. 
 
J Am Ceram Soc, 2007, 90(12): 3915–3922.
[44] GUERRERO A, GOÑI S, MACÍAS A, et al. 
 
Hydraulic activity and microstructural 
 
characterization of new fly ash-belite cements 
 
synthesized at different temperatures [J]. J 
 
Mater Res, 1999, 14(6): 2680–2687.
[45] GUERRERO A, GOÑI S, MORAGUES A, et al. 
 
Microstructure and mechanical performance of 
 
belite cements from high calcium coal fly ash 
 
[J]. J Am Ceram Soc. 2005, 88(7): 1845–1853.
[46] GOÑI S, GUERRERO A. Study of alkaline 
 
hydrothermal activation of belite cements by 
 
thermal analysis [J]. J Therm Anal 
 
Calorimetry, 2009, 99(2): 471–477.
[47] GUERRERO A, GOÑI S, DOLADO J S. Belite 
 
cements modifications of calcium silicate 
 
hydrate (C-S-H) gel by alkaline hydrothermal 
 
activation[J]. ACI Mater, 2009, 106(2): 138–
 
143.
[48] GOÑI S, GUERRERO A. Hydraulic activity 
 
of belite cement from class C coal fly ash. 
 
Effect of curing and admixtures [J]. Mater 
 
Constr, 2006, 56(283): 61–77.
[49] GOÑI S, GUERRERO A. Modifications of 
 
the C-S-H gel by hydration at 40ºC of belite 
 
cements from coal fly ash Class C [J]. J Am 
 
Ceram Soc, 2008, 91 (1): 209–214.
[50] GUERRERO A, GOÑI S, ALLEGRO V R. 
 
Durability of class C fly ash belite cement in 
 
simulated sodium chloride radioactive liquid 
 
waste: Influence of temperature [J]. J Hazard 
 
Mater, 2009, 162(2-3): 1099–1102.
[51] GUERRERO A, GOÑI S, ALLEGRO V R. 
 
Resistance of class C fly ash belite cement to 
 
simulated sodium sulphate radioactive liquid 
 
waste attack [J]. J Hazard Mater, 2009, 161(2
 
-3): 1250–1254.
[52] GUERRERO A, GOÑI S, MACÍAS A, 
 
Durability of new fly ash-belite cement 
 
mortars in sulfated and chloride medium [J]. 
 
Cem Concr Res, 2000, 30(8): 1231–1238.
[53] GUERRERO A, GOÑI S, ALLEGRO V R. 
 
Effect of temperature on the durability of 
 
class C fly ash belite cement in simulated 
 
radioactive liquid waste: Synergy of chloride 
 
and sulphate ions [J]. J Hazard Mater, 2009, 
 
165(1-3): 903–908.
[54] MCCARTHY M J, JONES M R, ZHENG L, et 
 
al. Characterising long-term wet-stored fly 
 
ash following carbon and particle size 
 
separation[J]. Fuel, 2013, 111: 430–441.
my wife cheated on me now what men and women husband cheat
open reasons why married men cheat My husband cheated on me
abortion las vegas abortion clinics in the bronx abortion pictures
amoxicillin amoxicillin amoxicillin
abortion pill abortion pill abortion pill
cialis discount coupons coupons for cialis 2016 cialis 2015 coupon
服务与反馈:
文章下载】【加入收藏
中国硅酸盐学会《硅酸盐学报》编辑室
京ICP备10016537号-2
京公网安备 11010802024188号
地址:北京市海淀区三里河路11号    邮政编码:100831
电话:010-57811253  57811254    
E-mail:jccs@ceramsoc.com