Ca0.7Sr0.3MoO4:Eu3+红色荧光粉发光性能的改进

作者：耿秀娟陈永杰肖林久杨英谢颖

关键词：红色荧光粉水热合成钼酸钙锶电荷补偿

分类号：O 482.31

出版年,卷(期):页码：2015,43(7):959-962

DOI：10.14062/j.issn.0454-5648.2015.07.17

摘要：

采用水热法制备了Ca0.70Sr0.18MoO4:Eu0.083+, Ca0.70Sr0.18−1.5xMoO4:Eu0.083+，Lax3+与Ca0.70Sr0.18−yMoO4:Eu0.083+, La0.043+, Nay+红色荧光粉。用X射线衍射、扫描电子显微镜、荧光分光光度计对样品的物相、形貌以及发光性能进行测试和表征。结果表明：La3+离子的共掺杂可显著增强Eu3+离子的发光性能。当La3+的掺杂量为4％(摩尔分数)时，在395 nm激发下，位于616 nm处的主发射峰的相对发光强度最大。另外，电荷补偿剂Na+的引入，也明显增强了荧光粉的发光强度，荧光粉的最高发光强度是未引入Na+荧光粉的1.47倍。

The red phosphors of Ca0.70Sr0.18MoO4:Eu0.083+, Ca0.70Sr0.18−1.5xMoO4:Eu0.083+, Lax3+ and Ca0.70Sr0.18−yMoO4: Eu0.083+, La0.043+, Nay+ were prepared by a hydrothermal method. The crystalline phase, morphology and luminescence characteristics of the phosphor particles were characterized by X-ray diffraction, scanning electron microscopy and fluorophotometry, respectively. The results show that the luminescence properties of Eu3+ ions can be evidently improved by co-doping of La3+ ions. When the doping mole fraction of La3+ is 4%, the relative luminous intensity at 616 nm main emission peak is maximum under the excitation of 395 nm. In addition, the incorporation of doping charge compensators Na+ can improve the luminescence intensity of phosphors. The maximum emission intensity is 1.47 times greater than that of phosphor without charge compensation.

基金项目：

辽宁省博士科研启动基金(20141079)项目。

作者简介：

耿秀娟(1975—)，女，博士，副教授。

参考文献：

[1] NARENDRAN N, DENG L. Characterizing LEDs for general illumination applications: Mixed-color and phosphor-based white sources [J]. Proc SPIE, 2001, 44: 137–147.

[2] MUTHU S, PASSHLEY M. IEEE J. Red, green and blue LED based white light generation: Issues and control [J]. IEEE J Sel Top Quantum Electron, 2002, 8: 327–333.

[3] WANG Z L, LIANG H B, GONG M L, et al. Novel red phosphor of Bi3+, Sm3+ coactivated NaEu(MoO4)2 [J]. Opt Mater, 2007, 29: 896–900.

[4] WANG Z L, LIANG H B, GONG M L, et al. Luminescence investigation of Eu3+ activated double molybdates red phosphors with scheelite structure [J]. J Alloy Compd, 2007, 432: 308–312.

[5] GAO F, LIANG L F, GUO C F. Preparation and luminescence of red light-emitting phosphors based on Li3Ba2Ln(3−x)Eux(MoO4)8 by sol-gel method [J]. Chin J Lumin (in Chinese), 2009, 30(5): 610–616.

[6] ZHANG R X, WANG H B, HUANG R X, et al. Preparation and package performances of red phosphor for LED [J]. Chin J Lumin (in Chinese), 2010, 31(3): 305–10.

[7] GENG X J, CHEN Y J, TIAN Y W, et a1. Luminescence and energy transfer in the red-emitting phosphor system Ca0.70Sr0.12MoO4:0.08Eu3+, 0.04Tb3+ [J]. Adv Mater Rapid Commun, 2014, 8(1/2): 30–32.

[8] GENG X J, TIAN Y W, CHEN Y J, et a1. Luminescence properties and energy transfer process of Sm3+–Eu3+ co-doped molybdate red-emitting phosphors by hydrothermal method [J]. Appl Phys B: Laser Opt, 2012, 107(1): 177–181.

[9] YANG X, GENG X J, LI Z Y, et al. Influence of flux on properties of CaSrMoO4:Eu3+ red phosphor [J]. J Electron Compon Mater (in Chinese), 2014, 33(12): 45–48.

[10] SHI W M, CHEN J F, GAO S K. Preparation and characterization of red-luminescence phosphors Ca0.5Sr0.5MoO4:Eu3+ for white-light-emitting diodes [J]. J Chin Ceram Soc, 2011, 39(2): 219–222.

[11] WANG F X, YUAN X M, XIE A, et al. Effect of Sr2+ content on luminescence characteristics of Ca0.85-xSrxMoO4:Eu0.0753+,Li0.075+ red-emitting Phosphors [J]. J Rare Earths (in Chinese), 2011, 29(2): 190–194.

[12] LI P L, WANG Z J, YANG Z P. Influence of charge compensation on the spectra characteristics of Sr2SiO4:Eu3+ phosphor [J]. Acta Photon Sin (in Chinese), 2008, 37(12): 2511–2514.

服务与反馈：

【文章下载】【加入收藏】