复合增强型SiO2气凝胶的一步法快速制备与性能表征

作者: margin-right:0cm margin-bottom:6.0pt  margin-left:0cm mso-para-margin-top:0cm mso-para-margin-right:0cm mso-para-margin-bottom: .5gd mso-para-margin-left:0cm line-height:12.0pt mso-line-height-rule:exactly  mso-pagination:none tab-stops:right231.0pt">  mso-ascii-font-family:" TimesNewRoman"  mso-hansi-font-family:" TimesNewRoman"   mso-font-width:85% mso-no-proof:yes">刘光武 TimesNewRoman"  serif mso-fareast-font-family:仿宋_GB2312  mso-font-width:85% mso-no-proof:yes">1 2 mso-ascii-font-family:" TimesNewRoman"  mso-hansi-font-family:" TimesNewRoman"   mso-font-width:85% mso-no-proof:yes">  TimesNewRoman"  serif mso-fareast-font-family:仿宋_GB2312  mso-font-width:85% mso-no-proof:yes"> mso-ascii-font-family:" TimesNewRoman"   mso-hansi-font-family:" TimesNewRoman"  mso-font-width:85% mso-no-proof:yes">斌 TimesNewRoman"  serif mso-fareast-font-family: 仿宋_GB2312 mso-font-width:85% mso-no-proof:yes">2 mso-ascii-font-family:" TimesNewRoman"   mso-hansi-font-family:" TimesNewRoman"  mso-font-width:85% mso-no-proof:yes"> 倪星元 TimesNewRoman"  serif mso-fareast-font-family: 仿宋_GB2312 mso-font-width:85% mso-no-proof:yes">2 mso-ascii-font-family:" TimesNewRoman"   mso-hansi-font-family:" TimesNewRoman"  mso-font-width:85% mso-no-proof:yes"> 刘燕刚 TimesNewRoman"  serif mso-fareast-font-family: 仿宋_GB2312 mso-font-width:85% mso-no-proof:yes">1 TimesNewRoman"  serif mso-fareast-font-family:华文仿宋  mso-font-width:85%"> 
单位:1. 上海交通大学药学院 上海 200040 2. 同济大学 上海市特殊人工微结构材料与技术重点实验室 上海 200092 
关键词:复合二氧化硅气凝胶 纤维增强 一步法 超疏水 保温隔热 
分类号:TQ174
出版年,卷(期):页码:2015,43(7):0-0
DOI:10.14062/j.issn.0454-5648.2015.07.13
摘要:

 以水玻璃为前驱体,去离子水为溶剂,经溶胶凝胶反应形成陶瓷纤维(15%)增强的SiO2湿凝胶,采用乙醇/三甲基氯硅烷/正己烷的混合液进行一步溶剂替换和表面基团改性后,经常压干燥制备出复合SiO2气凝胶块体。该复合气凝胶密度低(0.216 g/cm3)、成形性好,经高温处理后仍保持未开裂块状。样品与纤维复合后,纤维与SiO2气凝胶网络结合较好,复合材料的孔洞保持完整,骨架未发生断裂,基本保持较明显的海绵状网络结构和球形骨架结构。通过对气凝胶样品进行微观结构和比表面积分析、热重和疏水性测试、弹性模量及热导率表征,测得复合SiO2气凝胶的比表面积为743 m2/g,疏水接触角为146°,弹性模量为5.1 MPa。当温度升至400 ℃时,该气凝胶的热导率从0.026 3 W/(m·K)增加到0.051 2 W/(m·K),疏水接触角为138°。此外,对一步法涉及的溶剂替换及表面修饰机理也进行了分析。

 A composite of silica hydrogel with ceramic fibers (15% in mass fraction) was synthesized with sodium silicate as a precursor and deionized water as a solvent by a sol−gel method, and the composite was subsequently modified with a solution of ethanol/trimethylchlorosilane/n-hexane via one-step solvent exchange and surface modification, thus obtaining the crack-free and high hydrophobic composite aerogel monoliths. The composite aerogel has a low density of 0.216 g/cm3 and a superior formability. The ceramic fibers can be dispensed into the sample and combined with the silica aerogel network. There is a spongy meshwork structure on the surface of the aerogel. The aerogel samples were characterized by microstructure, analysis, specific surface area measurement, thermogravimetric analysis, hydrophobicity, elastic modulus and thermal conductivities test, respectively. The results show that the specific surface area of the composite aerogel is 743 m2/g, the contact angle with water is 146°, and the elastic modulus is 5.1 MPa. After a thermal process in the temperature range from room temperature to 400 , the hydrophobicity remains unchanged (about 138°), and the thermal conductivity of composite aerogel monoliths changes from 0.026 3 W/(m·K) to 0.051 2 W/(m·K). In addition, the mechanisms of solvent exchange and surface modification were also discussed.

printable coupons for cialis outbackuav.com coupon for free cialis
cialis coupon cialis coupon cialis coupon
bystolic copay card click bystolic coupon voucher
基金项目:
基金项目:国家自然科学基金(21172145, 21372152, 21402117)项目。
作者简介:
第一作者:刘光武(1985—),男,博士,讲师。
参考文献:
printable coupons for cialis drug discount coupons coupon for free cialis
doxycycline doxycycline doxycycline
服务与反馈:
文章下载】【加入收藏
中国硅酸盐学会《硅酸盐学报》编辑室
京ICP备10016537号-2
京公网安备 11010802024188号
地址:北京市海淀区三里河路11号    邮政编码:100831
电话:010-57811253  57811254    
E-mail:jccs@ceramsoc.com