YBa2Cu3O7–δ纳米点的制备及其对超导磁通钉扎性能的影响
作者:岳建设 李祯 赵琴 
单位:咸阳师范学院化学与化工学院 陕西 咸阳 712000 
关键词:钇钡铜氧 超导性 磁通钉扎 超导薄膜 
分类号:TB34
出版年,卷(期):页码:2017,45(1):0-0
DOI:10.14062/j.issn.0454-5648.2017.01.21
摘要:

为了提高YBa2Cu3O7–δ(YBCO)超导薄膜在磁场作用下的载流能力,首先使用YBCO前驱体溶液在LaAlO3单晶基板上制备了钉扎中心。通过改变YBCO前驱体溶液的浓度,改变基板上YBCO钉扎中心的尺寸和密度。然后在YBCO纳米点上表面外延生长YBCO薄膜。分析了YBCO在纳米点上生长膜层的取向、织构,研究了YBCO纳米点的磁通定扎效果。结果表明:使用0.1 mol/L的低浓度YBCO前驱体溶液可以获得细小的,尺寸约为30 nm且分布均匀的YBCO纳米点;在其上沉积的YBCO薄膜具有良好的织构,其磁通钉扎效果最明显,表现出了良好的抗磁场效应。随着YBCO前驱体浓度的增加,钉扎中心的尺寸逐渐增大,对YBCO厚膜的磁通钉扎效果逐渐衰减。不同浓度YBCO前驱体制备的纳米点对YBCO厚膜的外延生长没有影响。
 

In order to increase the current capacity of YBa2Cu3O7–δ (YBCO) superconductor in a magnetic field, the pinning central on the LaAlO3 crystal substrate was prepared with YBCO precursor solution, and the size and density were adjusted at various concentrations of YBCO precursor solution. The YBCO films on the YBCO nanodots surface were epitaxially grown. The growth orientation and texture of YBCO film were analyzed, and the magnetization behavior of YBCO film was investigated. The results show that the tiny and uniform YBCO nanodots with the size of 30 nm can be synthesized at the YBCO precursor solution of 0.1 mol/L concentration. A great thickness YBCO film deposited on these nanodots has a good texture, and the flux pinning effect increases, showing a good anti-magnetic field effect. The size of flux pinning central increases and the effect of flux pinning decreases with the increase of YBCO precursor concentration. The nanodots fabricated at different concentrations of YBCO precursor have no effect on the epitaxial growth of thick YBCO film.
 

基金项目:
陕西省教育厅专项科研项目(15JK1801);咸阳师范学院专项科研基金(13XSYK019,13XSYK020)。
作者简介:
岳建设(1980—),男,博士,讲师。
参考文献:

[1] AUGIERI A, CELENTANO G, GALLUZZI V, et al. Pinning analyses on epitaxial YBa2Cu3O7-δ films with BaZrO3 inclusion[J]. J Appl Phys, 2010, 108(6): 063906(1–5).
[2] KIM C J, YOON J S, NO K, et al. Enhanced flux pinning and formation of Ba4Y2CuMoOy in top-seeded melt growth processed YBa2Cu3O7–δ superconductors with Mo additions[J]. Supercond Sci Technol, 2010, 23(12): 125009(1–6).
[3] 侯艳荣,王大友,潘熙锋,等. MgB2块材的制备及磁通钉扎性能研究进展[J]. 材料导报,2014, 28(2): 12–16.
HOU Yanrong, WANG Dayou, PAN Xifeng, et al. Mater Rev (in Chinese), 2014, 28(2): 12–16.
[4] 王伟元,张辉,陈清明,等. YBa2Cu4O8超导材料及其制备技术的研究进展[J]. 热加工工艺,2014, 43(16): 16–22.
WANG Weiyuan, ZHAN Hui, CHENG Qingming, et al. Hot Working Technol (in Chinese), 2014, 43(16): 16–22.
[5]` CRISAN A, FUJIWARA S, NIE J C, et al. Sputtered nanodots: A costless method for inducing effective pinning centers in superconducting thin films[J]. Appl Phys Lett, 2001, 79(27): 4547–4549.
[6] SARKAR A, MIKHEENKO P, DANG V S, et al. Enhancing critical current in YBCO thick films: Substrate decoration and quasi-superlattice approach [J]. Physica C, 2009, 469: 1550–1553.
[7] 汪薪生,郭峰,任泽龙,等. YBCO/ND-Y2O3/YBCO 超导薄膜的制备及其特性研究[J]. 人工晶体学报, 2015, 44(7): 1731–1735.
WANG X S, GUO F, REN Z L, et al. J Synth Cryst (in Chinese), 2015, 44(7): 1731–1735.
[8] BIAN W B, CHEN Y Q, LI M J, et al. Ultralow-fluorine sol-gel deposition of thick YBCO multilayer films[J]. J Sol-Gel Sci Technol, 2015, 75(3): 574–581.
[9] 武传宝,赵高扬,雷黎,等. Y2O3缓冲层对YBCO超导转变温度的影响[J]. 低温物理学报, 2014, 36(2): 81–85.
WU C B, ZHAO G Y, LEI L, et al. Chin J Low Temp Phys (in Chinese), 2014, 36(2): 81–85.
[10] SARKAR A, DANG V S, MIKHEENKO P, et al. Improved critical current densities in thick YBa2Cu3O7–δ multilayer films interspaced with non-superconducting YBa2Cu3Ox nanodots[J]. Thin Solid Films, 2010, 519(2): 876–879.
[11] 杨坚. YBCO涂层导体长带与厚膜制备技术及钉扎机制研究[D]. 北京: 北京有色金属研究总院, 2013.
YANG Jian. Research on fabrication of long length YBCO coated conductor and flux pinning mechanism for thick film (in Chinese, dissertation). Beijing: General Research Institute for Nonferrous Metals, 2013.

服务与反馈:
文章下载】【加入收藏
中国硅酸盐学会《硅酸盐学报》编辑室
京ICP备10016537号-2
京公网安备 11010802024188号
地址:北京市海淀区三里河路11号    邮政编码:100831
电话:010-57811253  57811254    
E-mail:jccs@ceramsoc.com