无固化剂的环氧树脂乳液对油井水泥早期水化的影响
作者:阎培渝1 岳蕾1 代丹2 罗宇维2 
单位:1. 清华大学土木工程系 北京 100084 2. 中海油田服务股份有限公司 河北 燕郊 065201 
关键词:环氧树脂乳液 水泥浆 水化过程 水化产物 抗压强度 
分类号:TE256
出版年,卷(期):页码:2017,45(5):1-6
DOI:10.14062/j.issn.0454-5648.2017.05.00
摘要:

 将不同聚合度的环氧树脂乳液,以不同掺量掺加到固井水泥浆中,制备环氧树脂乳液改性水泥浆。在无固化剂、不同温度条件下,通过水化热测量,扫描电子显微镜,X射线衍射等方法研究了环氧树脂乳液对油井水泥早期水化特性的影响。结果表明:相对于纯油井水泥浆体,环氧树脂水泥浆的水化进程被延缓,但是水化产物没有明显变化,环氧树脂在硬化水泥浆体中主要以聚合物膜的形式存在,可填充水泥石内部的毛细孔隙,使环氧树脂水泥石的抗压强度随着环氧树脂掺量的提高而略有增加。

 

 Epoxy resin modified cement pastes containing different percentages of emulsion were prepared using two kinds of epoxy resin emulsions with different polymerization degrees. The influence of epoxy resin emulsion without curing agent on the early hydration process of oil well cement pastes was investigated at different temperatures using isothermal hydration heat evolution, scanning electron microscopy and X-ray diffraction. The results show that the hydration process of epoxy resin modified cement pastes is delayed, compared to that of blank cement pastes, while their hydration products are similar. There is an epoxy resin film wrapping the particles in hardened cement pastes, which can fill the capillary pores of cement stones. Hence, the compressive strength of cement stones increases slightly as the content of epoxy resin emulsion increases.

 
基金项目:
国家自然科学基金项目(No. 51678344,No. 51678343)。
作者简介:
阎培渝(1955—),男,博士,教授。
参考文献:

 [1]Syed T, Cutler T. Well Integrity Technical and Regulatory Considerations for CO2 Injection Wells[C]//SPE International Conference on Health, Safety and Environment in Oil and Gas Exploration and Production. Society of Petroleum Engineers, 2010.

[2]Detroit W J, Sanford M E, Chatterji J, et al. Oil well cementing process: US, USRE31190[P]. 1983.
[3]李铭. 聚合物改性水泥基材料研究[D]. 武汉工程大学, 2012.
LI Ming. Wuhan Institute of Technology, 2012.
[4]方萍. 丙苯乳液改性聚合物水泥力学性能和内部结构研究[J]. 混凝土, 2001(3): 46–48.
FANG Ping. Concrete (in Chinese), 2001(3): 46–48.
[5]陈友治, 李方贤, 王红喜. 水乳环氧对水泥砂浆强度的影响[J]. 重庆大学学报: 自然科学版, 2003, 26(12): 48–50.
CHEN Youzhi, LI Fangxian, WANG Hongxi. J Chongqing Univ: Sci Technol (in Chinese), 2003, 26(12): 48–50.
[6]沈凡, 黄绍龙, 孙政, 等. 水性环氧树脂-水泥-乳化沥青复合胶结体系的硬化机理[J]. 中南大学学报: 自然科学版, 2012, 43(1): 105–110.
SHEN Fan, HUANG Shaolong, SUN Zheng, et al. J Central South Univ: Sci Technol, 2012, 43(1): 105–110.
[7]OTA M, OHKUBO T, OCHI M, OHAMA Y. Strength development through long-term dry curing of initially combind wet/dry-cured and steam-cured hardener-free epoxy-modified mortars[J]. J Struc Construct Eng (in Japanese), 2011, 76(663): 875–880.
[8]Ariffin N F, Hussin M W, Sam A R M, et al. Strength properties and molecular composition of epoxy-modified mortars[J]. Construct Build Mater, 2015, 94: 315–322.
服务与反馈:
文章下载】【加入收藏
中国硅酸盐学会《硅酸盐学报》编辑室
京ICP备10016537号-2
京公网安备 11010802024188号
地址:北京市海淀区三里河路11号    邮政编码:100831
电话:010-57811253  57811254    
E-mail:jccs@ceramsoc.com