2CaO·2SrO·3Al2O3·SO3的形成动力学
作者:赵九野 常钧 
单位:大连理工大学土木工程学院 辽宁 大连 116024 
关键词:硫铝酸锶钙 动力学 Rietveld定量方法 形成过程 
分类号:TQ172
出版年,卷(期):页码:2017,45(8):1128-1135
DOI:
摘要:

 研究了一种硫铝酸锶钙矿物2CaO·2SrO·3Al2O3·SO3(C2Š2A3$)的形成过程,采用Rietveld定量方法确定了不同温度、不同保温时间下烧成熟料中C2Š2A3$矿物的含量,并对C2Š2A3$的形成过程进行动力学分析。结果表明:在1 150–1 350 ℃条件下,熟料中C2Š2A3$的含量随着保温时间的延长而增加,在1 350 ℃保温180 min时C2Š2A3$的含量达到97.3%;在1 400 ℃保温超过30 min时,熟料中C2Š2A3$的含量开始减少;在1 450 ℃熟料中C2Š2A3$的含量随保温时间的延长而降低。形成C2Š2A3$的固相反应符合三维扩散模型,Jander模型具有最好的拟合效果。C2Š2A3$形成过程的活化能为479 kJ/mol。烧成温度主要影响C2Š2A3$矿物颗粒的细观形貌,但不会影响C2Š2A3$矿物的元素分布及组成。

 

 The formation process of 2CaO·2SrO·3Al2O3·SO3, which is a type of Sr-bearing ye’elimite, was investigated. The content of C2Š2A3$ in clinkers sintered in different temperatures and prolong time was determined via the Rietveld quantitative phase analysis. The formation process follows the kinetic models. The results show that the content of C2Š2A3$ increases with increasing the holding time at 1 150–1 350 ℃, and the content of C2Š2A3$ is 97.3% in clinkers at 1 350 ℃ for 180 min. C2Š2A3$ starts to decompose at 1 400 ℃ when prolong time exceeds 30 min. The content of C2Š2A3$ decreases with increasing the holding time at 1 450 ℃. The solid-phase reaction of C2Š2A3$ formation fits the three-dimensional diffusion model, and the Jander model gives the optimal fitting results. The activation energy of C2Š2A3$ is 479 kJ/mol. The sintering temperature affects the mesoscopic morphology of C2Š2A3$ particles, while does not affect the elementary distribution and component.

 
基金项目:
国家自然科学基金(51472041)资助项目。
作者简介:
赵九野(1989—),男,博士研究生。
参考文献:

 [1] Teoreanu I, Muntean M, Dragnea I. Type 3(CaO·Al2O3)·Mx (SO4)y compounds and compatibility relations in CaO-CaO·Al2O3·Mx (SO4)y systems[J]. Cement, 1986, 83: 39–46.

[2] Feng X, Cheng X. The structure and quantum chemistry studies of 3CaO·3Al2O3·SrSO4[J]. Cem Concr Res, 1996, 26(6): 955–962.
[3] 程新, 冯修吉. 应用量子化学方法研究钙矾石的强度特性[J]. 武汉工业大学学报, 1995(04): 12–14.
CHENG Xin, FENG Xiuji. J Wuhan Univ Technol (in Chinese), 1995(04): 12–14.
[4] Yan P. Hydration of Sr- and Ba-bearing sulphoaluminates in the presence of sulphates[J]. Adv Cem Res, 1993, 5(18): 65–69.
[5] 常钧, 谭文杰, 黄睿, 等. 硫铝酸锶钙矿物的研究. 硅酸盐学报[J]. 2010, 38(4): 666–670.
CHANG Jun, TAN Wenjie, HUANG Rui, et al. J Chin Ceram Soc, 2010, 38(4): 666–670.
[6] 谭文杰. 硫铝酸锶钙水泥及耐久性的研究[D]. 济南: 济南大学, 2011.
TAN Wenjie. Research on calcium strontium sulphoaluminate cement and its durability (in Chinese, dissertation). Jinan: Jinan University, 2011.
[7] 谭文杰, 常钧, 吴昊泽, 等. 锶渣为原料制备硫铝酸锶钙水泥的研究[C]//中国硅酸盐学会水泥分会首届学术年会, 中国河南焦作, 2009.
TAN Wenjie, CHANG Jun, WU Haoze, et al. Research on calcium strontium sulphoaluminate cement with strontium slag as raw material (in Chinese)[C]//The first academic year in the Chinese society of silicate cement branch. China, Henan, Jiaozuo, 2009.
[8] Khawam A, Flanagan D  R. Solid-state kinetic models: basics and mathematical fundamentals[J]. J Phys Chem B. 2006, 110(35): 17315.
[9] 胡荣祖, 高胜利, 赵凤起. 热分析动力学(第二版)[M]. 北京: 科学出版社, 2008: 4–5.
[10] Chang J, Zhao J, Shang X, et al. Rietveld refinement for Sr(Ba)-bearing ye'elimite[J]. Adv Cem Res, 2016, 28(9): 583–594.
[11] Lazic B, Krüger H, Kahlenberg V, et al. Incommensurate structure of Ca2Al2O5 at high temperatures - structure investigation and Raman spectroscopy[J]. Acta Crystallogr, 2008, 64(4): 417–425.
[12] Jacobsen S D, Smyth J R, Swope R J, et al. Rigid-body character of the SO4 groups in celestine, anglesite and barite[J]. Canad Mineral, 1998, 36(4): 1053–1060.
[13] Schulze A R, Mueller-Buschbaum H. Zur struktur von monoklinem SrAl2O4[J]. Zeitschrift fuer Anorganische Allgemeine Chem, 1981(475): 205–210.
[14] Bernuylopez C, Allix M, Bridges C A, et al. Sr2MgMoO6-δ: structure, phase stability, and cation site order control of reduction[J]. Chem Mater, 2007, 19: 1035–1043.
[15] Wyckoff R W G. Crystal Structures[M]. New York: Interscience Publishers, 1963: 85–237.
[16] Wang X L, Hubbard C R, Alexander K B, et al. Neutron diffraction measurements of the residual stresses in Al2O3-ZrO2(CeO2) ceramic composites[J]. J Am Ceram Soc, 2005, 77(6): 1569–1575.
[17] 马素花, 沈晓冬, 黄叶平, 等. 无水硫铝酸钙矿物的合成及形成机制(英文)[J]. 硅酸盐学报. 2008(1): 78–81.
MA Suhua, SHENG Xiaodong, HUANG Yeping, et al. J Chin Ceram Soc, 2008(1): 78–81.
[18] Nishino T, Yamauchi E. Cation Exchange Reaction between Sulfate and Carbonate of Alkaline Earth[J]. J Ceram Assoc Jpn, 1983, 91(1050): 62–67.
[19] Ramach V S. Handbook of thermal analysis of construction Materials[M]. Published by Elsevier Inc, 2002: 35–69.
[20] Li X, Zhang Y, Shen X, et al. Kinetics of calcium sulfoaluminate formation from tricalcium aluminate, calcium sulfate and calcium oxide[J]. Cem Concr Res, 2014, 55: 79–87.
[21] Huang Y, Wang S, Gong C, et al. Study on isothermal formation dynamics of calcium barium sulphoaluminate mineral[J]. J Inorg Organomet Polym Mater, 2013, 23(23): 1172–1176.
[22] 王丽, 李金洪, 杨静. 高温固硫物相硫铝酸钙在不同气氛下的动力学实验研究[J]. 矿物岩石, 2009(03): 23–28.
WANG Li, LI Jinhong, YANG Jing. J Mineral Petrol (in Chinese), 2009(03): 23–28.
[23] ALI M M, GOPAL S, HANDOO S K. Studies on the formation kinetics of calcium sulphoaluminate[J]. Cem Concr Rese, 1994, 24(4): 715–720.
服务与反馈:
文章下载】【加入收藏
中国硅酸盐学会《硅酸盐学报》编辑室
京ICP备10016537号-2
京公网安备 11010802024188号
地址:北京市海淀区三里河路11号    邮政编码:100831
电话:010-57811253  57811254    
E-mail:jccs@ceramsoc.com