ZnO–B2O3掺杂BaAl2Si2O8陶瓷的结构及微波介电性能

作者：黄龙丁士华严欣堪宋天秀张云张晓云

关键词：钡长石单斜相晶体结构介电性能

分类号：TQ174

出版年,卷(期):页码：2019,47(6):0-0

DOI：

摘要：

采用固相反应法制备BaAl2Si2O8–x%ZnO–B2O3(x=0,1,2,3,4,质量分数)陶瓷。探究了不同含量的ZnO–B2O3(ZB)烧结助剂对BaAl2Si2O8(BAS)陶瓷的烧结温度、结构及微波介电性能的影响。结果表明：ZB烧结助剂可降低BAS陶瓷的烧结温度。并且能够促进BAS晶体结构由六方相转变为单斜相，当x=1时，六方相BAS全部转变为单斜相BAS，并且ZB烧结助剂添加量在4%以内，无第二相生成。添加1%的ZB烧结助剂可促进样品晶粒长大，密度、介电常数和品质因数增大，谐振频率温度系数的绝对值减小。在x=1，烧结温度为1 350 ℃时，能够获得品质因数较高的单斜相BAS，其介电性能为：εr=6.45，Q×f=40 608 GHz，τf=–22.46×10–6 K–1。

BaAl2Si2O8 ceramics with a samll amount of ZnO–B2O3 (ZB) as sintering additives were prepared by solid-state sintering. The sintering temperature, structure and microwave dielectric properties of BaAl2Si2O8 (BAS) with ZB were investigated. The results show that the ZB sintering additives can reduce the sintering temperature and promote the transition of crystal structure of BAS. As x =1, all the hexacelsian transforms into celsian, and the second phase does not appear as x≤4. The sintering additives of 1%ZB can promote the grain growth, increase the bulk density, dielectric constant and Q×f value, and decrease the absolute value of τf. The BAS with 1%ZB sintered at 1 350 ℃ shows a high Q×f of 40 608 GHz, and the dielectric properties are εr=6.45 and τf = –22.46×10–6 K–1.

基金项目：

教育部春晖计划(Z2011077)；四川省特种材料及制备技术重点实验室开放课题资助项目(szjj2017-059)；四川省教育厅资助项目(14ZB0126)；四川省粉末冶金工程技术中心资助项目(SC-FMYJ2017-04，SC-FMYJ2017-07)；国家自然科学基金(11074203)；西华大学研究生创新基金(ycjj2018012，ycjj2018013)。

作者简介：

参考文献：

[1] SONG X Q, LU W Z, WANG X C, et al. Sintering behaviour and microwave dielectric properties of BaAl2–2x(ZnSi)xSi2O8 ceramics[J]. J Eur Ceram Soc, 2018, 38(4): 1529–1534.

[2] LANSMANN V, JANSEN M. Application of the glass–ceramic process for the fabrication of whisker reinforced celsian-composites[J]. J Mater Sci, 2001, 36(6): 1531–1538.

[3] BAHAT D. Kinetic study on the hexacelsian-celsian phase transformation[J]. J Mater Sci, 1970, 5(9): 805–810.

[4] YOSHIKI B, MATSUMOTO K. High–Temperature modification of barium feldspar[J]. J Am Ceram Soc, 1951, 34(9): 283–286.

[5] YANG X J, ZHANG Y, DING S H, et al. Structure and dielectric properties of Ca doped BaAl2Si2O8[J]. Ceram Int, 2018, 44: S43–S45.

[6] CHEN M, LEE W E, JAMES P F. Synthesis of monoclinic celsian glass–ceramic from alkoxides[J]. J Non–Cryst Solids, 1992, 147: 532–536.

[7] HAN L C, DING S H, SONG T X, et al. ZBAS on the structure and dielectric property of BaAl2Si2O8[J]. J Inorg Mater, 2018, 33(8): 883–888.

[8] KIM J R, KIM D W, CHO I S, et al. Low temperature sintering and microwave dielectric properties of Ba3Ti5Nb6O28 with ZnO–B2O3 glass additions for LTCC applications[J]. J Eur Ceram Soc, 2007, 27(8–9): 3075–3079.

[9] LEE Y C, LEEB W H, SHIEUC F S. Microwave dielectric properties and microstructures of Ba2Ti9O20-based ceramics with 3ZnO–B2O3 addition[J]. J Eur Ceram Soc, 2005, 25(15): 3459–3468.

[10] KIM D W, LEE D G, HONG K S. Low-temperature firing and microwave dielectric properties of BaTi4O9 with Zn–B–O glass system[J]. Mater Res Bull, 2001, 36(3–4): 585–595.

[11] YANG H, LI E, YANG H, et al. Synthesis of Zn0.5Ti0.5NbO4 microwave dielectric ceramics with Li2O–B2O3–SiO2 glass for LTCC application[J]. Int J Appl Glass Sci, 2018, 9(3): 392–402.

[12] SHIH Y T, JEAN J H. Low–fire processing of microwave (Ca1–xSrx)(Zr1–yMny)O3 dielectric with Li2O–B2O3–SiO2 glass in H2/N2[J]. Ceram Int, 2017, 43: S306–S311.

[13] YOON K H, PARK M S, CHO J Y, et al. Effect of B2O3–Li2O on microwave dielectric properties of (Ca0.275Sm0.4Li0.25)TiO3 ceramics[J]. J Eur Ceram Soc, 2003, 23(14): 2423–2427.

[14] LEE K T, ASWATH P B. Role of mineralizers on the hexacelsian to celsian transformation in the barium aluminosilicate (BAS) system[J]. Mater Sci Eng A, 2003, 352(1): 1–7.

[15] HYATT M J, BANSAL N P. Crystal growth kinetics in BaOAl2O3•2SiO2 and SrOAl2O3•2SiO2 glasses[J]. J Mater Sci, 1996, 31(1): 172–184.

[16] LI E, NIU N, WANG J, et al. Effect of Li–B–Si glass on the low temperature sintering behaviors and microwave dielectric properties of the Li-modified ss–phase Li2O–Nb2O5–TiO2 ceramics[J]. J Mater Sci: Mater Electron, 2015, 26(5): 3330–3335.

[17] ZHANG S, SU H, ZHANG H, et al. Microwave dielectric properties of CaWO4–Li2TiO3 ceramics added with LBSCA glass for LTCC applications[J]. Ceram Int, 2016, 42(14): 15242–15246.

[18] KIM J R, KIM D W, JUNG H S, et al. Low-temperature sintering and microwave dielectric properties of Ba5Nb4O15 with ZnB2O4 glass[J]. J Eur Ceram Soc, 2006, 26(10–11): 2105–2109.

服务与反馈：

【文章下载】【加入收藏】