氧化铝夹杂高温变形过程中的破碎机理
作者: style='WHITE-SPACE: normal  WORD-SPACING: 0px  POSITION: relative  TEXT-TRANSFORM: none  COLOR: rgb(124 124 124)  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  PADDING-LEFT: 0px  ORPHANS: 2  WIDOWS: 2  MARGIN: 0px 0.5em  LETTER-SPACING: normal  PADDING-RIGHT: 0px  BACKGROUND-COLOR: rgb(255 255 255)  TEXT-INDENT: 0px  -webkit-text-stroke-width: 0px  font-stretch: normal'> onclick="                            TurnPageToKnet('au' '金淼' '09296110')                           " style='CURSOR: pointer  TEXT-DECORATION: none  COLOR: rgb(102 102 102)  OUTLINE-WIDTH: medium  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  OUTLINE-STYLE: none  PADDING-LEFT: 0px  MARGIN: 0px  OUTLINE-COLOR: invert  PADDING-RIGHT: 0px  BACKGROUND-COLOR: transparent  font-stretch: normal'>金淼 杨帅 style='WHITE-SPACE: normal  WORD-SPACING: 0px  POSITION: relative  TEXT-TRANSFORM: none  COLOR: rgb(124 124 124)  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  PADDING-LEFT: 0px  ORPHANS: 2  WIDOWS: 2  MARGIN: 0px 0.5em  LETTER-SPACING: normal  PADDING-RIGHT: 0px  BACKGROUND-COLOR: rgb(255 255 255)  TEXT-INDENT: 0px  -webkit-text-stroke-width: 0px  font-stretch: normal'> onclick="                            TurnPageToKnet('au' '陈雷' '10255143')                           " style='CURSOR: pointer  TEXT-DECORATION: none  COLOR: rgb(102 102 102)  OUTLINE-WIDTH: medium  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  OUTLINE-STYLE: none  PADDING-LEFT: 0px  MARGIN: 0px  OUTLINE-COLOR: invert  PADDING-RIGHT: 0px  BACKGROUND-COLOR: transparent  font-stretch: normal'>陈雷 style='WHITE-SPACE: normal  WORD-SPACING: 0px  POSITION: relative  TEXT-TRANSFORM: none  COLOR: rgb(124 124 124)  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  PADDING-LEFT: 0px  ORPHANS: 2  WIDOWS: 2  MARGIN: 0px 0.5em  LETTER-SPACING: normal  PADDING-RIGHT: 0px  BACKGROUND-COLOR: rgb(255 255 255)  TEXT-INDENT: 0px  -webkit-text-stroke-width: 0px  font-stretch: normal'> onclick="                            TurnPageToKnet('au' '郭宝峰' '09296012')                           " style='CURSOR: pointer  TEXT-DECORATION: none  COLOR: rgb(102 102 102)  OUTLINE-WIDTH: medium  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  OUTLINE-STYLE: none  PADDING-LEFT: 0px  MARGIN: 0px  OUTLINE-COLOR: invert  PADDING-RIGHT: 0px  BACKGROUND-COLOR: transparent  font-stretch: normal'>郭宝峰 class=icon-email style="HEIGHT: 9px  WIDTH: 14px  BACKGROUND: url(../images/icon-email.png) no-repeat  PADDING-BOTTOM: 0px  FONT-STYLE: normal  PADDING-TOP: 0px  PADDING-LEFT: 0px  MARGIN: 0px  DISPLAY: inline-block  PADDING-RIGHT: 0px"> style='WHITE-SPACE: normal  WORD-SPACING: 0px  POSITION: relative  TEXT-TRANSFORM: none  COLOR: rgb(124 124 124)  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  PADDING-LEFT: 0px  ORPHANS: 2  WIDOWS: 2  MARGIN: 0px 0.5em  LETTER-SPACING: normal  PADDING-RIGHT: 0px  BACKGROUND-COLOR: rgb(255 255 255)  TEXT-INDENT: 0px  -webkit-text-stroke-width: 0px  font-stretch: normal'> onclick="                            TurnPageToKnet('au' '卢昀' '44099189')                           " style='CURSOR: pointer  TEXT-DECORATION: none  COLOR: rgb(102 102 102)  OUTLINE-WIDTH: medium  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  OUTLINE-STYLE: none  PADDING-LEFT: 0px  MARGIN: 0px  OUTLINE-COLOR: invert  PADDING-RIGHT: 0px  BACKGROUND-COLOR: transparent  font-stretch: normal'>卢昀 style='WHITE-SPACE: normal  WORD-SPACING: 0px  POSITION: relative  TEXT-TRANSFORM: none  COLOR: rgb(124 124 124)  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  PADDING-LEFT: 0px  ORPHANS: 2  WIDOWS: 2  MARGIN: 0px 0.5em  LETTER-SPACING: normal  PADDING-RIGHT: 0px  BACKGROUND-COLOR: rgb(255 255 255)  TEXT-INDENT: 0px  -webkit-text-stroke-width: 0px  font-stretch: normal'> onclick="                            TurnPageToKnet('au' '张胜利' '39048666')                           " style='CURSOR: pointer  TEXT-DECORATION: none  COLOR: rgb(102 102 102)  OUTLINE-WIDTH: medium  PADDING-BOTTOM: 0px  TEXT-ALIGN: center  PADDING-TOP: 0px  FONT: 14px/1.4 Arial  "Microsoft Yahei"  宋体  OUTLINE-STYLE: none  PADDING-LEFT: 0px  MARGIN: 0px  OUTLINE-COLOR: invert  PADDING-RIGHT: 0px  BACKGROUND-COLOR: transparent  font-stretch: normal'>张胜利 
单位:燕山大学机械工程学院 
关键词:氧化铝  夹杂物  高温变形  破碎强度  Z参数  破碎机理  
分类号:TQ174.758.11
出版年,卷(期):页码:2020,48(6):833-840
DOI:10.14062/j.issn.0454-5648.2020.06.20190598
摘要:
以性质近似于钢锭中Al2O3夹杂的高温烧结Al2O3块体为研究对象,采用专门的热压缩装置,通过高温压缩实验研究了Al2O3在变形过程中的破碎行为,结合破碎样品断口特征分析,建立了基于双曲正弦形式Arrhenius方程的Al2O3高温破碎强度预测模型,构建了以Z参数作表征的Al2O3破碎模式区域图,揭示了不同变形参数下Al2O3的破碎机理。结果表明:Al2O3热压缩过程呈现为典型的脆性断裂,其破碎强度与应变速率呈正相关,与变形温度呈负相关,且对变形温度更敏感。随着Z参数的减小,Al2O3夹杂破碎模式逐渐由穿晶断裂转变为沿晶断裂。
基金项目:
国家自然科学基金(51675465);
作者简介:
参考文献:
服务与反馈:
文章下载】【加入收藏
中国硅酸盐学会《硅酸盐学报》编辑室
京ICP备10016537号-2
京公网安备 11010802024188号
地址:北京市海淀区三里河路11号    邮政编码:100831
电话:010-57811253  57811254    
E-mail:jccs@ceramsoc.com